An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Metallic Glasses in Cell Phones Angelika Franz

  2. what is a metallic glass structure properties processing cell phone cases cell phone hinges Outline

  3. Metallic Glass I • amorphous material: atoms “frozen” in non-crystalline form • lack long-range atomic order • first formed in 1957 by Duwez by rapid quenching • gold-silicon alloy • only very thin, small samples could be produced (order or micrometers)

  4. Metallic Glass II • 1990: found new alloys to form bulk metallic glasses • typically used three or more metallic elements • cooling rates needed decreased • could produce samples on order of centimeters Zr-Ti-Cu-Ni-Al alloy

  5. Structure I • first believed atoms were randomly packed together densly like hard spheres in a liquid • solvent atoms randomly arranged with solute atoms fitting into open cavities • now believe short-range, even medium-range order exists in materials

  6. Structure II • form nanoscale “superclusters” • difference in size between alloyed elements make solvent atoms cluster around solute atoms • Kasper polyhedra: 7 to 15 atoms arranged around central atom • polyhedra shape depends on size of constituent atoms • range of coordination numbers: different polyhedra exist within same material

  7. Structure III • was proposed that clusters conform to fcc lattice for closest-packing with strain factor to limit order to 1-1.5 nm • actually found clusters pack into icosahedral structures usually 1.5 nm wide • creates cavities into which extra solute atoms can pack

  8. Properties I • lack of crystallinity means lack of defects • gives rise to interesting properties • stronger and lighter than metals • tough: resistant to fracture • unlike ceramic glass is not brittle • easily heated, softened and molded into shapes

  9. Properties II • uncorrosive • not transparent • very high elastic strain limit • makes material bouncy

  10. Processing I • formed by quenching at rates of 1-100 degrees Celsius per second • used to be 1 million degrees Celsius per second • prevent atoms from forming into crystalline structure, instead freeze into liquid-like structure • limits size and shape of material produced

  11. Processing II • near net-shape casting • alloy is cast near to final shape • injection molding • metallic glass is heated until it softens and can flow into the mold • physical vapor deposition • ion irradiation • mechanical alloying

  12. Cell Phone Cases I • alloy of zirconium, titanium, copper, nickel and beryllium • produced using near net-shape casting • smaller, thinner designs with greater protection of internal components

  13. Cell Phone Cases II • sleek metallic surface • scratch and corrosion resistant • ~2.5 times strength of titanium alloy • ~1.5 times hardness of stainless steel • non-reactive • thinner walls with greater strength

  14. Cell Phone Hinges • deformation resistant • high yield strength and elasticity • more durable than conventional materials • very resilient to impact and daily wear-and-tear • reliable in repeated load-bearing conditions

  15. References • http://www.liquidmetal.com/ • http://www.jhu.edu/news/home06/jan06/glass.html • http://engr.oregonstate.edu/momentum/stories/liquid_metal.html • http://www.jhu.edu/matsci/people/faculty/hufnagel/background.html • http://www.nature.com/nature/journal/v439/n7075/full/439405a.html;jsessionid=396A417548AD57212FA5DAF138B540CA • http://www.sciencedaily.com/releases/1998/03/980331074950.htm • B. Van Aken, P. de Hey, and J. Sietsma: Structural relaxation and plastic flow in amorphous La50Al25Ni25. Mater. Sci. Eng. A278, 247 (2000). • http://www.sciwrite.caltech.edu/journal03/owensmichael.html