Development of Photocatalytic Active TiO 2 Surfaces by Thermal Spraying of Nanopowders

Development of Photocatalytic Active TiO 2 Surfaces by Thermal Spraying of Nanopowders. Authors: Filofteia-Laura Toma, Ghislaine Bertrand, Didier Klein, Cathy Meunier, and Sylvie Begin [1] Presented by: Gregory D. Holland October 19, 2010 Oklahoma City Community College.

marlow
Télécharger la présentation

Development of Photocatalytic Active TiO 2 Surfaces by Thermal Spraying of Nanopowders

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Development of Photocatalytic Active TiO2 Surfaces by Thermal Spraying of Nanopowders Authors: Filofteia-Laura Toma, Ghislaine Bertrand, Didier Klein, Cathy Meunier, and Sylvie Begin [1] Presented by: Gregory D. Holland October 19, 2010 Oklahoma City Community College

  2. Outline of Presentation • The Problem: NOx • Titanium dioxide • Sources • Uses • Experimental method • Spraying methods • Feedstock materials • Experimental results • Characterization • Conclusions Photo: http://www.germes-online.com

  3. The Problem • Nearly 15 million people in the U.S. have asthma.[2] • Concentrations of NOx as low as 0.1 ppm cause lung irritation and a measurable decrease in the lung function of asthmatics.[3] • Many major cities in the U.S. average more than 100 days a year when ambient NOx levels exceed 0.1 ppm for at least an hour (e.g. Denver, Detroit, El Paso, Phoenix, St. Louis).[4]

  4. TiO2 Photocatalysis Image: http://www.noodor.net/

  5. Titanium Dioxide Sources • Naturally occurring minerals: • Rutile - purified using a chloride process • Anatase • Brookite • Synthesized from other naturally occurring minerals: • Ilmenite (FeTiO3) - Iron removed using a sulfuric acid process Photo: http://www.hummingbirdminerals.com Naturally occurring, acicular crystals of rutile.

  6. Titanium Dioxide Uses • Primarily used as white pigment in: • Toothpaste • Paint • Sunscreen • Cosmetics • Foods • Paper • And more! Photo: http://pamdora.com Photo: http://www.enviroblog.org/ http://www.jwodcatalog.com

  7. Experimental Purpose • Evaluate TiO2 Photocatalytic degradation of gaseous nitrogen oxide pollutants (NO, NOx) • Compare different spraying methods • Compare different feed materials • Characterize coating microstructure to help explain difference in effectiveness: • Scanning electron microscopy (SEM) • X-ray diffraction (XRD)

  8. Plasma Spraying Setup

  9. Experimental Method Three different thermal spraying techniques compared: • Atmospheric plasma spraying (APS) Sulzer-Metco PTF4 plasma gun • Primary gas: Argon • Secondary gases: H2 and He • Suspension plasma spray (SPS) Custom design with peristaltic pump • Primary gas: Argon • Solvents: Distilled water (WSC) or ethanol (ASC) • High-velocity oxygen fuel (HVOF) Sulzer-Metco CDS 100 gun • Fuel gas: Methane with oxygen

  10. Experimental Method Three commercial feed stocks compared: • TiO2–ST01: 100% anatase (7 nm crystals), forming spherical particle agglomerates (10 – 50 μm) • TiO2–PC105: 100% anatase (23 nm crystals) • TiO2–P25: 80% anatase (25 nm crystals) and 20% rutile (50 nm) crystals

  11. Degradation Tests • Custom-built chamber • 0.4 grams of powder covering 54 cm2 surface • 15-W daylight lamp with 30% UVA and 4% UVB • NO and NOx concentrations measured continuously • Performances evaluated by: • Note: Initial concentrations not specified

  12. Degradation Results

  13. Characterization Results

  14. Characterization Results

  15. Characterization Results • Original feedstock compositions for comparison: • TiO2–ST01: 100% anatase (7 nm crystals), forming spherical particle agglomerates (10 – 50 μm) • TiO2–PC105: 100% anatase (23 nm crystals) • TiO2–P25: 80% anatase (25 nm crystals) and 20% rutile (50 nm) crystals

  16. Conclusions Based on Results • Aqueous suspension sprays (WSC) outperformed APS and HVOF methods, probably due to lower process temperatures • Higher anatase composition • Smaller crystallite size • Aqueous suspensions of ST01 and P25 outperformed the raw powders • Not explained by anatase composition • May be due to higher hydroxylation of the surfaces

  17. The Bottom Line • Initial studies suggest aqueous suspension plasma spraying may be an appropriate technique for producing active titania surfaces for the photocatalytic reduction of reactive gaseous pollutants such as nitrogen oxides. • Additional questions related to cost, durability, and fouling of the coatings still need to be addressed.

  18. References [1] Filofteia-Laura Toma, Ghislaine Bertrand, Didier Klein, Cathy Meunier, and Sylvie Begin, “Development of Photocatalytic Active TiO2 Surfaces by Thermal Spraying of Nanopowders,” Journal of Nanomaterials, vol. 2008, Article ID 384171, 8 pages, (2008). doi:10.1155/2008/384171 [2] Stephen Redd, “Asthma in the United Stated: Burden and Current Theories,” Environmental Health Perspectives, vol. 110, supp. 4, pp. 557-560, (2008). [3] Wisconsin Department of Natural Resources, “Nitrogen Oxide Sources and Health Effects,” http://dnr.wi.gov/air/aq/pollutant/oxides.htm, (March 23, 2010). [4] United States Environmental Protection Agency, “Risk and Exposure Assessment to Support the Review of the NO2 Primary National Ambient Air Quality Standard,” EPA document # EPA-452/R-08-008a, November 2008. Questions?