CHAPTER 36 - MICROFABRICATION TECHNOLOGIES

CHAPTER 36 - MICROFABRICATION TECHNOLOGIES. Microsystem Products Microfabrication processes Nanotechnology. Trends and Terminology. Trend: miniaturization of products and parts, with features sizes measured in microns (10 -6 m) Some of the terms:

nevaeh
Télécharger la présentation

CHAPTER 36 - MICROFABRICATION TECHNOLOGIES

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. CHAPTER 36 - MICROFABRICATION TECHNOLOGIES • Microsystem Products • Microfabrication processes • Nanotechnology ISE 316 - Manufacturing Processes Engineering

  2. Trends and Terminology • Trend: miniaturization of products and parts, with features sizes measured in microns (10-6 m) • Some of the terms: • Microelectromechanicalsystems (MEMS) - miniature systems consisting of both electronic and mechanical components • Microsystem technology (MST) - refers to the products as well as the fabrication technologies • Nanotechnology - even smaller devices whose dimensions are measured in nanometers (10-9 m) ISE 316 - Manufacturing Processes Engineering

  3. Advantages of Microsystem Products • Less material usage • Lower power requirements • Greater functionality per unit space • Accessibility to regions that are forbidden to larger products • In most cases, smaller products should mean lower prices because less material is used ISE 316 - Manufacturing Processes Engineering

  4. Types of Microsystem Devices • Microsensors • Microactuators • Microstructures and microcomponents • Microsystems and micro-instruments ISE 316 - Manufacturing Processes Engineering

  5. Microsensors A sensor is a device that detects or measures some physical phenomenon such as heat or pressure • Most microsensors are fabricated on a silicon substrate using the same processing technologies as those used for integrated circuits • Microsensors have been developed for measuring force, pressure, position, speed, acceleration, temperature, flow, and a variety of optical, chemical, environmental, and biological variables ISE 316 - Manufacturing Processes Engineering

  6. Microactuators An actuator converts a physical variable of one type into another type, and the converted variable usually involves some mechanical action • An actuator causes a change in position or the application of force • Examples of microactuators: valves, positioners, switches, pumps, and rotational and linear motors ISE 316 - Manufacturing Processes Engineering

  7. Microstructures and Microcomponents Micro-sized parts that are not sensors or actuators • Examples: microscopic lenses, mirrors, nozzles, and beams • These items must be combined with other components in order to provide a useful function ISE 316 - Manufacturing Processes Engineering

  8. Microsystems and micro-instruments Integration of several of the preceding components with the appropriate electronics package into a miniature system or instrument • They tend to be very application specific • Examples: microlasers, optical chemical analyzers, and microspectrometers • The economics of manufacturing these kinds of systems have tended to make commercialization difficult ISE 316 - Manufacturing Processes Engineering

  9. Industrial Applications of Microsystems • Ink-jet printing heads • Thin-film magnetic heads • Compact disks • Automotive components • Medical applications • Chemical and environmental applications • Other applications ISE 316 - Manufacturing Processes Engineering

  10. Ink-Jet Printing Heads • Currently one of the largest applications of MST • A typical ink-jet printer uses up several cartridges each year • Today’s ink-jet printers have resolutions of 1200 dots per inch (dpi) • This resolution converts to a nozzle separation of only about 21 m, certainly in the microsystem range ISE 316 - Manufacturing Processes Engineering

  11. Figure 37.3 - Diagram of an ink-jet printing head ISE 316 - Manufacturing Processes Engineering

  12. Thin-Film Magnetic Heads • Read-write heads are key components in magnetic storage devices • Reading and writing of magnetic media with higher bit densities are limited by the size of the read-write head • Development of thin-film magnetic heads was an important breakthrough not only in digital storage technology but microfabrication technologies as well • Thin-film read-write heads are produced annually in hundreds of millions of units, with a market of several billion dollars per year ISE 316 - Manufacturing Processes Engineering

  13. Figure 37.4 - Thin-film magnetic read-write head (simplified) ISE 316 - Manufacturing Processes Engineering

  14. Compact Disks • Important commercial products, as storage media for audio, video, and computer software • Mass-produced by plastic molding of polycarbonate • The molds are made using microsystem technology • A master for the mold is made from a smooth thin layer of photosensitive polymer on a glass plate • The polymer is exposed to a laser beam that writes the data into the surface • The mold is then made by electroforming metal onto this polymer master ISE 316 - Manufacturing Processes Engineering

  15. Automotive Components • Micro-sensors and other micro-devices are widely used in modern automobiles • There are between 20 and 100 sensors installed in a modern automobile, depending on make and model • Functions include electronic engine control, cruise control, anti-lock braking systems, air bag deployment, automatic transmission control, power steering, all-wheel drive, automatic stability control, on-board navigation systems, and remote locking and unlocking • In 1970 there were virtually no on-board sensors ISE 316 - Manufacturing Processes Engineering

  16. Medical Applications • A driving force for microscopic devices is the principle of minimal-invasive therapy, which means using very small incisions or even available body orifices to access the medical problem of concern • Standard medical practice today is to use endoscopic examination accompanied by laparoscopic surgery for hernia repair and removal of organs such as gall bladder and appendix • Growing use of similar procedures is expected in brain surgery, operating through one or more small holes drilled through the skull ISE 316 - Manufacturing Processes Engineering

  17. Microfabrication Processes • Many MST products are based on silicon • Reasons why silicon is a desirable material in MST: • Microdevices often include electronic circuits, so both the circuit and the device can be made on the same substrate • Silicon has good mechanical properties: high strength & elasticity, good hardness, and relatively low density • Techniques to process silicon are well-established ISE 316 - Manufacturing Processes Engineering

  18. Other Materials and MST Processing • MST often requires other materials in addition to silicon to obtain a particular microdevice • Example: microactuators often consist of several components made of different materials • Thus, microfabrication techniques consist of more than just silicon processing: • LIGA process • Other conventional and nontraditional processes accomplished on a microscopic scale ISE 316 - Manufacturing Processes Engineering

  19. Silicon Layer Processes • First application of silicon in MST was in the fabrication of piezoresistive sensors to measure stress, strain, and pressure in the early 1960s • Silicon is now widely used in MST to produce sensors, actuators, and other microdevices • The basic processing technologies are those used to produce integrated circuits • However, there are certain differences between the processing of ICs and the fabrication of microdevices ISE 316 - Manufacturing Processes Engineering

  20. Differences between Microfabrication and IC Fabrication • Aspect ratios (height-to-width ratio of the features) in microfabrication are generally much greater than in IC fabrication • The device sizes in microfabrication are often much larger than in IC processing • The structures produced in microfabrication often include cantilevers and bridges and other shapes requiring gaps between layers ISE 316 - Manufacturing Processes Engineering

  21. Figure 37.5 - Aspect ratio (height-to-width ratio) typical in (a) fabrication of integrated circuits and (b) microfabricated components ISE 316 - Manufacturing Processes Engineering

  22. 3D Features in Microfabrication • Chemical wet etching of polycrystalline silicon is isotropic, with the formation of cavities under the edges of the resist • However, in single-crystal Si, etching rate depends on the orientation of the lattice structure • 3-D features can be produced in single-crystal silicon by wet etching, provided the crystal structure is oriented to allow the etching process to proceed anisotropically ISE 316 - Manufacturing Processes Engineering

  23. Figure 37.6 - Three crystal faces in the silicon cubic lattice structure: (a) (100) crystal face, (b) (110) crystal face, and (c) (111) crystal face ISE 316 - Manufacturing Processes Engineering

  24. Bulk Micromachining to Achieve Large Aspect Ratios • Certain etching solutions, such as potassium hydroxide (KOH), have a very low etching rate in the direction of the (111) crystal face • This permits formation of distinct geometric structures with sharp edges in single-crystal Si if the lattice is oriented favorably • Bulk micromachining - relatively deep wet etching process on single-crystal silicon substrate • Surface micromachining - planar structuring of the substrate surface, using much more shallow etching ISE 316 - Manufacturing Processes Engineering

  25. Figure 37.7 - Several structures that can be formed in single-crystal silicon substrate by bulk micromachining: (a) (110) silicon and (b) (100) silicon ISE 316 - Manufacturing Processes Engineering

  26. Bulk Micromachining to Create Thin Membranes in a Microstructure • A method is needed to control the etching penetration into the silicon, so as to leave a membrane layer • A common method is to dope the Si substrate with boron atoms, which reduces the etching rate of Si • Epitaxial deposition is then used to apply an upper layer of silicon so it will have the same single-crystal structure and lattice orientation as the substrate • Boron doping to establish the etch resistant layer of silicon is called the “p+ etch-stop technique” ISE 316 - Manufacturing Processes Engineering

  27. Figure 37.7 - Formation of a thin membrane in a silicon substrate: (1) silicon substrate is doped with boron, (2) a thick layer of silicon is applied on top of the doped layer by epitaxial deposition, (3) both sides are thermally oxidized to form a SiO2 resist on the surfaces, (4) the resist is patterned by lithography, and (5) anisotropic etching is used to remove the silicon except in the boron doped layer ISE 316 - Manufacturing Processes Engineering

  28. Cantilevers, Overhangs, and Similar Structures • Surface micromachining can be used to construct cantilevers, overhangs, and similar structures on a silicon substrate • The cantilevered beams are parallel to but separated by a gap from the silicon surface • Gap size and beam thickness are in the micron range ISE 316 - Manufacturing Processes Engineering

  29. Figure 37.9 - Surface micromachining to form a cantilever: (1) on the silicon substrate is formed a silicon dioxide layer, whose thickness will determine the gap size for the cantilevered member; (2) portions of the SiO2 layer are etched using lithography; (3) a polysilicon layer is applied; (4) portions of the polysilicon layer are etched using lithography; and (5) the SiO2 layer beneath the cantilevers is selectively etched ISE 316 - Manufacturing Processes Engineering

  30. Lift-Off Technique in Microfabrication A procedure to pattern metals such as platinum on a substrate • These structures are used in certain chemical sensors, but are difficult to produce by wet etching • Dry etching provides anisotropic etching in almost any material • Dry etching - material removal by the physical and/or chemical interaction between an ionized gas and the atoms of a surface exposed to the gas ISE 316 - Manufacturing Processes Engineering

  31. Figure 37.10 - The lift-off technique: (1) resist is applied to substrate and structured by lithography, (2) platinum is deposited onto surfaces, and (3) resist is removed, taking with it the platinum on its surface but leaving the desired platinum microstructure ISE 316 - Manufacturing Processes Engineering

  32. LIGA Process • An important technology of MST • Developed in Germany in the early 1980s • The letters LIGA stand for the German words • Lithographie(in particular X-ray lithography) • Galvanoformung (translated electrodeposition or electroforming) • Abformtechnik (plastic molding) • The letters also indicate the LIGA process sequence ISE 316 - Manufacturing Processes Engineering

  33. Figure 37.10 - LIGA processing steps: (1) thick layer of resist applied and X-ray exposure through mask, (2) exposed portions of resist removed, (3) electrodeposition to fill openings in resist, (4) resist stripped to provide (a) a mold or (b) a metal part ISE 316 - Manufacturing Processes Engineering

  34. Advantages and Disadvantages of LIGA • LIGA is a versatile process – it can produce parts by several different methods • High aspect ratios are possible (large height-to-width ratios in the fabricated part) • A wide range of part sizes are feasible, with heights ranging from micrometers to centimeters • Close tolerances are possible • Disadvantage: LIGA is a very expensive process, so large quantities of parts are usually required to justify its application ISE 316 - Manufacturing Processes Engineering

  35. Ultra-High Precision Machining • Trends in conventional machining include taking smaller and smaller cut sizes • Enabling technologies include: • Single-crystal diamond cutting tools • Position control systems with resolutions as fine as 0.01 m • Applications: computer hard discs, photocopier drums, mold inserts for compact disk reader heads, high-definition TV projection lenses, and VCR scanning heads ISE 316 - Manufacturing Processes Engineering

  36. Ultra-High Precision Machining – An Example • One reported application: milling of grooves in aluminum foil using a single-point diamond fly-cutter • The aluminum foil is 100 m thick • The grooves are 85 m wide and 70 m deep ISE 316 - Manufacturing Processes Engineering

  37. Figure 37.11 - Ultra-high precision milling of grooves in aluminum foil ISE 316 - Manufacturing Processes Engineering

  38. Microstereolithography (MSTL) • Layer thickness in conventional STL = 75 m to 500 m, MSTL layer thickness = 10 to 20 m typically, with even thinner layers possible • Laser spot size diameter in STL is around 250 m, MSTL spot size is as small as 1 or 2 m • Another difference: work material in MSTL is not limited to a photosensitive polymer • Researchers report success in fabricating 3-D microstructures from ceramic and metallic materials • The difference is that the starting material is a powder rather than a liquid ISE 316 - Manufacturing Processes Engineering

  39. Nanotechnology Next generation of even smaller devices and their fabrication processes to make structures with feature sizes measured in nanometers (1 nm = 10-9 m) • Structures of this size can almost be thought of as purposely arranged collections of individual atoms and molecules • Two processing technologies expected to be used: • Molecular engineering • Nanofabrication - similar to microfabrication only performed on a smaller scale ISE 316 - Manufacturing Processes Engineering

  40. Molecular Engineering Additive processes that build the nanostructure from its molecular components • Nature provides a guide for the kinds of fabrication techniques that might be used • In molecular engineering and in nature, entities at the atomic and molecular level are combined into larger entities, proceeding in a constructive manner toward the creation of some deliberate thing ISE 316 - Manufacturing Processes Engineering

  41. Molecular Engineering - continued • If the thing is a living organism, the intermediate entities are biological cells, and the organism is grown through an additive process that exhibits massive replication of individual cell formations • Similar approaches are being explored for fabricating nanostructures other than living organisms ISE 316 - Manufacturing Processes Engineering

  42. Nanofabrication Technologies Processes similar to those used in the fabrication of ICs and microsystems, but carried out on a scale several orders of magnitude smaller than in microfabrication • The processes involve the addition, alteration, and subtraction of thin layers using lithography to determine the shapes in the layers • Applications: transistors for satellite microwave receivers, lasers used in communications systems, compact disc players ISE 316 - Manufacturing Processes Engineering

  43. Nanofabrication Technologies - continued • A significant difference is the lithography technologies that must be used at the smaller scales in nanofabrication • Ultraviolet photolithography cannot be used effectively, owing to the relatively long wavelengths of UV radiation • Instead, the preferred technique is high-resolution electron beam lithography, whose shorter wavelength virtually eliminates diffraction during exposure ISE 316 - Manufacturing Processes Engineering