Table Ⅶ : The table of peak current

Table Ⅶ : The table of peak current. Fig 2. The renewing test of Au electrode WE: Adsorbed Au-Cr coated on silicone wafer by e-beam, 0.125 cm 2 , RE: SCE, CE: Pt, Electrolyte: 0.2 M H2SO4, Scan range: -0.20 ~0.60 V , Scan rate: 0.05 V/sec. Fig 2. The cyclic voltammetry of Au electrode

novia
Télécharger la présentation

Table Ⅶ : The table of peak current

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Table Ⅶ: The table of peak current

  2. Fig 2. The renewing test of Au electrode WE: Adsorbed Au-Cr coated on silicone wafer by e-beam, 0.125 cm2, RE: SCE, CE: Pt, Electrolyte: 0.2 M H2SO4, Scan range: -0.20~0.60 V, Scan rate: 0.05 V/sec

  3. Fig 2. The cyclic voltammetry of Au electrode WE: Au-Cr coated on silicone wafer by e-beam, 0.125 cm2, RE: Ag/AgCl(0.5MKCl), CE: Pt, Electrolyte: 0.5 M KCl +20 mM K4Fe(CN)6+20 mM K3Fe(CN)6), Scan range: -0.20~0.60 V, Scan rate: 0.05 V/sec

  4. Table Ⅶ: The table of peak current *normal concentration interference/0.5 MKCl/PH=3.51(1N HCl) *8ppm albumin /0.5MKCl/PH=3.51(1N HCl) *adsorb temperature 37-38℃