1 / 20

Ferromagnetic semiconductors for spintronics

Ferromagnetic semiconductors for spintronics. Kevin Edmonds, Kaiyou Wang, Richard Campion, Devin Giddings, Nicola Farley, Tom Foxon, Bryan Gallagher, Tomas Jungwirth School of Physics & Astronomy, University of Nottingham Mike Sawicki, Tomasz Dietl IFPAN, Warsaw, Poland

oriole
Télécharger la présentation

Ferromagnetic semiconductors for spintronics

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Ferromagnetic semiconductors for spintronics Kevin Edmonds, Kaiyou Wang, Richard Campion, Devin Giddings, Nicola Farley, Tom Foxon, Bryan Gallagher, Tomas Jungwirth School of Physics & Astronomy, University of Nottingham Mike Sawicki, Tomasz Dietl IFPAN, Warsaw, Poland Tarnjit Johal, Gerrit van der Laan Daresbury Laboratory

  2. Semiconductor spintronics Electron Spin Electron Charge Semiconductor Spintronics Photon Polarisation Benefits: Fast, small, low dissipation devices Quantum computation? New physics

  3. (Ga,Mn)As H. Ohno et al. (1996): ferromagnetism in GaAs thin films doped ~5% with Mn Growth by low temperature MBE to beat equilibrium solubility limit

  4. Carrier-mediated ferromagnetism Substitutional Mn is an acceptor and a J=5/2 magnetic moment. Mn: [Ar] 3d5 4s2 Ga: [Ar] 3d10 4s2 4p1 Ferromagnetism driven by antiferromagnetic exchange coupling Jp-d S.s between Mn moments and spin-polarised GaAs valence electrons Mn Carrier density determines the key magnetic properties of (Ga,Mn)As (e.g. TC, HC,...)

  5. Carrier-mediated ferromagnetism Photogenerated magnetism Koshihara PRL (1997) Spin-FET H. Ohno et al., Nature (2000) Vgate ħw InMnAs GaSb InMnAs B (mT)

  6. Curie temperatures Max. TC=172K (so far...) Wang et al., JAP ‘04

  7. Interstitial Mn: a magnetism killer Mn Yu et al., PRB ’02: ~10-20% of total Mn concentration is incorporated as interstitials Increased TC on annealing corresponds to removal of these defects. As Negative effects on magnetic order: compensating donor – reduces hole density antiferromagnetic coupling between interstitial and substitutional Mn predicted Blinowski PRB ‘03

  8. 1D diffusion process T=190oC Diffusion to free surface - activation energy  0.7eV Edmonds, Bogusławski et al., PRL 92, 037201 (2004)

  9. Magnetic moment and antiferromagnetic coupling X-ray absorption measurements, ALS line 4.0.2 and ESRF line ID8: XMCD asymmetry  30% Magnetic moment  2.3mB XMCD asymmetry  55% Magnetic moment  4.5mB

  10. Ferromagnetic moment vs. field in unannealed film at 6K: annealed B5/2(6K) B=2T B=5T as-grown B5/2(28K) AF coupling described by Teff = T + TAF = (6+22)K

  11. Ferromagnetic semiconductor heterostructures Protocols for growth of semiconductor heterostructures are well-established Addition of spin gives a new degree of freedom e.g. tunnelling structure (Ga,Mn)As AlAs (Ga,Mn)As Tanaka et al. (2001) 70% TMR Chiba et al. (2003) 400% Rüster et al. (2004) >100,000% !!

  12. Tunnelling Anisotropic Magnetoresistance [100] [100] AlOx Au (Ga,Mn)As [110] Gould et al., PRL (2004) TMR-like signal with in control sample with only one ferromagnetic contact Tunnelling probability depends on magnetisation direction of single layer (two step reversal process)

  13. Anisotropic magnetoresistance M I q Magnetoresistance on rotating M away from ‘x’ direction - strong function of Mn concentration, well described by mean-field model Jungwirth et al. APL ‘03

  14. TAMR in Nanoconstrictions 5nm (Ga,Mn)As film with 30nm wide constrictions Giant anisotropic magnetoresistance ~100% in tunnelling regime Giddings et al., cond-mat/0409209

  15. Ge 300K! GaAs GaSb InAs CB VB Mn 3d GaSb GaAs GaP GaN Prospects for room temperature ferromagnetism Predicted TC in (III,Mn)V semiconductors, if Mn is a shallow acceptor T. Dietl, Science ’00; JVSTB ‘03

  16. Ga1-xMnxN Small RT ferromagnetic signal superimposed on larger paramagnetic part (Sonoda ’01; Reed ’01; Thaler ’02; Biquard ’03 etc.) Most are n-type  results are inconsistent with carrier-mediated ferromagnetism Dietl Science ‘00 Several MnxNy magnetic phases exist Zajac et al. ‘03 Phase segregation?

  17. Cubic (Ga,Mn)N: a key to p-type conductivity Wurtzite (Ga,Mn)N is usually n-type; Mn ionisation energy ~1.4eV (Graf et al APL (2002)) But in zincblende (Ga,Mn)N/GaAs we observe robust p-type behaviour DEa~50meV Evidence for collective magnetic effects at low T: Novikov et al. Semicond. Sci. Tech. (2004)

  18. Conclusions  GaAs doped with ~% Mn is ferromagnetic – a model system for investigating magnetic phenomena in semiconductors- gate controlled magnetism - tunnelling magnetoresistance - new tunnelling effects prospects for semiconductors with room temperature ferromagnetism – but phase segregation may be an issue

  19. Magnetic anisotropy Strong cubic anisotropy with <100> easy axes, reduced to biaxial (in-plane) or uniaxial (perpendicular) due to strain. Weaker uniaxial anisotropy between in-plane [110] and [110] orientations, origin unknown. B// B

  20. Magnetic anisotropy rotation In-plane uniaxial easy axis rotates from [110] to [110] on increasing the carrier density above ~6 x 1020 cm-3 by annealing. Sawicki et al., PRB (submitted) easy axis [110 ] easy axis [110]