Desmear Process 除膠渣製程. 恆利肯有限公司 Hurricane chemical Co. Tel: 886-3-2127720 Fax: 886-3-3524476. Desmear 為除膠渣之意 , 主要目的是移除多層板因鑽孔後所留下的膠渣 (smear), 達到內層銅與孔銅導通 , 並防止孔銅拉離 . 除此之外能使孔壁粗化 , 以利後製程化學銅有更好的附著表面 . 除膠渣與後製程一次銅之關係. 原銅. 橫向玻璃纖維. 縱向玻璃纖維. 樹脂. 內層銅. Panel plating ( 一銅 ). 除膠渣流程.

ostinmannual
Télécharger la présentation

Desmear Process 除膠渣製程

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Desmear Process除膠渣製程 恆利肯有限公司 Hurricane chemical Co. Tel: 886-3-2127720 Fax: 886-3-3524476

  2. Desmear為除膠渣之意,主要目的是移除多層板因鑽孔後所留下的膠渣(smear),達到內層銅與孔銅導通,並防止孔銅拉離.除此之外能使孔壁粗化,以利後製程化學銅有更好的附著表面.Desmear為除膠渣之意,主要目的是移除多層板因鑽孔後所留下的膠渣(smear),達到內層銅與孔銅導通,並防止孔銅拉離.除此之外能使孔壁粗化,以利後製程化學銅有更好的附著表面.

  3. 除膠渣與後製程一次銅之關係 原銅 橫向玻璃纖維 縱向玻璃纖維 樹脂 內層銅 Panel plating (一銅)

  4. 除膠渣流程 膨鬆劑 水洗 水洗 水洗 除膠渣 回收 水洗 水洗 中和劑 水洗 水洗 (H2O2/H2SO4)

  5. 除膠渣後 樹脂 玻璃纖維

  6. 膨鬆劑 品名: D-810/D-800Z 目的: 是一鹼性添加劑,主要是切斷樹脂膠渣本身的聚 集鍵結,並加以膨鬆及軟化,以利高錳酸鉀的咬 蝕 參數: 1)濃度:D-810(35%)/D-800Z(4%) 2)溫度: 55~65℃ 3)時間: 5~6 min 4)消耗量: 5ml/SF 5)換槽頻率: 3000 SF/gal

  7. 環氧樹脂的形成反應機構 CH3 （苯二酚） HO OH + CH3 c 2CH2 CH—CH2 —CL O

  8. Difunctional Epoxy Resin H2C CH2 O 架橋基 架橋基 O CH HC CH2 CH2 CH3 CH3 O–CH2 – CH – CH2 – O – O C C O n OH CH3 CH3 高錳酸鉀主要攻擊基

  9. 常見的環氧樹脂架橋劑 NH Dicyandimide ( Dicy ) , H2NCNHCN 聯胺 (Diamine) , NH2•NH2 二乙三胺 ( Diethylenetriammine ), NH2(CH2)2NH2(CH2)2NH2

  10. 架橋反應式 • –NH2 + CH2—CH–→ –N: CH2—CH → –NH–CH2–CH– • 親核性攻擊反應 電子移轉 O H  OH H O

  11. 膨鬆原理 常見的膨鬆劑有醯胺類 (Amide) 與醇醚類 (Glycol Ether) 利用膨鬆劑與架橋劑反應 , 使環氧樹脂中的架橋鏈斷鍵 斷鍵之後的環氧樹脂結構變的鬆弛 , 達到軟化的目的

  12. 膨鬆反應機構 O –CH—CH2 —N: + C → –CH –CH2 + –NH –C –(CH2)4 –NH2 H   O  NH (CH2)4 H O O

  13. 除膠渣劑 品名: D-820A/D-820B 目的: 是一種鹼性高錳酸鉀溶液 , 可打斷樹脂系統中的 鍵結 , 將已膨鬆的樹脂膠渣除去 參數: 1)濃度:D-820A(50~70g/L)/D-820B (15%) 2)溫度: 65~75 ℃ 3)時間: 10~12 min 4)消耗量:D-820A(1.4g/SF)/D-820B(1.4ml/SF) 5)換槽頻率: 5000SF/gal

  14. 環氧樹脂的氧化分解機構 • MnO4¯+4H2O+3e¯MnO2+4OH ¯ E°=0.57V • 2KMnO4  K2MnO4 + MnO4 + O2 • –OCH2–CH –CHO – + 6KMnO4  3K2MnO4+ 3MnO2 + 3CO2 + 3H2O OH

  15. MnO4²¯再生法 EPR再生法: 4 MnO4²¯ + O2 +2H2O → 4MnO4¯ + OH ¯ 陽極反應: 2Mn(+6) + 2e¯→ 2Mn(+7) 4OH ¯ + 4e¯→ 2H2O + O2↑ 陰極反應: 4H(+) + 4e¯→ 3H2

  16. 中和劑 品名: D-830 目的: 主要是除去殘留於孔壁的二氧化錳及高 錳酸鉀鹽類物質,以利後製程的品質 參數: 1)濃度: D-830(15%) 2)溫度: 50~60 ℃ 3)時間: 5~6 min 4)消耗量: D-830(3.5ml/SF) / H2SO4(3ml/SF) 5)換槽頻率: 800SF/gal

  17. 中和反應方程式 2KMnO4 + 2NH2OH + 3H2SO4 →2MnSO4 + K2SO4 + 6H2O + N2 + O2 5K2MnO4 + 4NH2OH + 10H2SO4 →5MnSO4 + 5K2SO4 + 16H2O + 2N2 + 4O2 5MnO2+2NH2OH+5H2SO4 →5MnSO4 + 8H2O + N2 + 2O2

  18. Weight Loss Test 1.取25cm²大小的裸板(不含銅)兩片 2.洗淨 , 並烘烤110℃ , 10min 3.冷卻後 , 秤重至小數點下4位 , 記錄為w1 4.穿線綁於掛架上 , 走完除膠渣段 5.洗淨 , 並烘烤110℃ , 10min 6.冷卻後 , 秤重至小數點下4位 , 記錄為w2 7.計算: weight loss = 8.參考範圍: 0.15~0.35 mg/cm² W1-W2(mg) 長  寬  2 (25cm²)

  19. 設備 流程過濾 攪拌震盪器Tank材質加熱器材質 膨鬆槽   316,Ti,PE316, TI,Telfon WRX 3 AIR PP,PE 除渣槽 AIR  316, Ti SS,Ti 回收槽 PP,PE WRX 2 AIR PP,PE 中和槽  PP,PE Telfon WRX 2 AIR PP,PE