T6-6061 Aluminum Mockup of overlap joint. Short piece (< 0.5m) resting on foam insulation

T6-6061 Aluminum Mockup of overlap joint. Short piece (< 0.5m) resting on foam insulation. Gentle grinding: Max Temp < 50 C Aggressing grinding: Max Temp < 90 C. ~1 mm thick emery grinding wheel. Work done by Bert Gonzales Temperature monitoring: Jorge Montes. Monitor 1.

ramla
Télécharger la présentation

T6-6061 Aluminum Mockup of overlap joint. Short piece (< 0.5m) resting on foam insulation

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. T6-6061 Aluminum Mockup of overlap joint. Short piece (< 0.5m) resting on foam insulation Gentle grinding: Max Temp < 50 C Aggressing grinding: Max Temp < 90 C ~1 mm thick emery grinding wheel Work done by Bert Gonzales Temperature monitoring: Jorge Montes

  2. Monitor 1 Temperature (Celsius) versus time (arbitrary) Monitor 2 Monitor 3 Aggressive grinding at time ~ 500 Gentle grinding at time ~ 80

  3. Bert Gonzales reported that cutting through the weld was not any harder than cutting through T6-6061 Al Dremel tool kit also has a fiber-glass reinforced emery grinding wheel. Bert says that this is harder to control. It tends to jump a bit. Emery wheel is recommended.

  4. Type density Thermal Cond. Specific Heat T6-6061 Al* 2.7g/cc 167 W/(m-C) 1.3e3 J/(kg-C) Pure Al* 2.7g/cc 220 W/(m-C) 896 J/(kg-C) AA 1100** 2.7g/cc 222 W/(m-C) 906 J/(kg-C) If aggressively grinding the weld: Worse case temperature = (90 C – 24 C)*(1.3e3/900) + 24 C = 119 C If gently grinding the weld: Worse case temperature = (50 C – 24 C)*(1.3e3/900) + 24 C = 62 C *http://www.engineersedge.com/properties_of_metals.htm ** http://www.substech.com/dokuwiki/doku.php?id= wrought_aluminum_alloy_1100&DokuWiki=5fb40349ffd1dc8213525ba1dde42e6b