Solidification of electromagnetically levitated Nd-Fe-B melt droplets

Sino-German Workshop on EPM 10-12 October, 2004, Shanghai. Solidification of electromagnetically levitated Nd-Fe-B melt droplets. J. Gao 1,2 , T. Volkmann 1 , J. Strohmenger 1 , S. Reutzel 3 , D.M. Herlach 1 1 Institute of Space Simulation, German Aerospace Center, Cologne, Germany

ranae
Télécharger la présentation

Solidification of electromagnetically levitated Nd-Fe-B melt droplets

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Sino-German Workshop on EPM 10-12 October, 2004, Shanghai Solidification of electromagnetically levitated Nd-Fe-B melt droplets J. Gao1,2, T. Volkmann1, J. Strohmenger1, S. Reutzel3, D.M. Herlach1 1 Institute of Space Simulation, German Aerospace Center, Cologne, Germany 2 Key Laboratory of Electromagnetic Processing of Materials, Northeastern University, Shenyang, China 3 Institute of Experimental Physics IV, Ruhr-University of Bochum, Bochum, Germany

  2. Outline • Motivation • Experimental-Setup • Solidification experiments • Microstructural examination • Conclusions & outlook

  3. B 60 (BH)max 50 Nd-Fe-B 40 Ferrite 30 (BH)max H 20 0 10 0 1990 1940 1950 1960 1970 1980 Introduction to Nd-Fe-B alloys Nd2Fe14B (MGOe) Sm2Co17 max (BH) SmCo5 Ba-Ferrite DS-Alnico AlNiCo5 Year F-Nd2Fe14B cell Hysteresis loops Development of PMM

  4. L f g Peritectic formation of f Fabrication of sintered Nd-Fe-B magnets requires casting of bulk ingots for powder precursors. Peritectic formation of f Nd-Fe-B phase diagram Residual Fe dendrites lead to reduced magnetic properties.

  5. Overheated L g T(K) TL TP L+ g f TL 82.3 76.5 Undercooled f L+ f Fe (at.%) (Nd:B=2:1) Motivation - direct f formation Peritectic f-phase might be solidified directly from an undercooled liquid. It is a big challenge to undercool Nd-Fe-B melt droplets because of their high chemical reactivity!

  6. Electromagnetic Levitator To chart recorder Pyrometer Sample(1g, 6mm) R. F. Generator Coil Vac:=10-6 mbar PHe=10-50 mbar Quartz tube He (6N) To vacuum pump EML + low P + T>>TL large DT Nd2O3 (s)+ Nd (L) NdO (g)

  7. In-situ X-ray diffraction analysis X-ray Synchrotron radiation: highly penetrating Beamtime: ID 15A, ESRF, Grenoble, France

  8. Cooling curves during solidification Recalescence occurs due to rapid latent heat release!

  9. In-situ diffraction analysis MS= c-Nd2Fe17Bx; Th2Zn17-type rhombohedral structure; Decomposition of Nd2Fe17Bx into Fe plus Nd2Fe14B.

  10. Primary phase selection map ●g-Fe ■f-Nd2Fe14B ♦c-Nd2Fe17Bx

  11. Solidification microstructure

  12. Thermomagnetic analysis

  13. Summary • Chemically reactive Nd-Fe-B melt droplets could be undercooled by electromagnetic levitation under controlled conditions. • Solidification of levitated Nd-Fe-B droplets depends on melt undercooling, and three metastable solidification pathways have been determined for Nd-rich compositions.

  14. Outlook – Fe-rich compositions Preliminary drop tube experiments Fe phase is not harmful any longer! EM-levitation for in-situ studies.