1 / 15

Brick Manufacture

Brick Manufacture. Carlos Brown, Corey Henriquez, Michael Berry, R.J. Lavigne The Knack 11/30/10. Basic Brick Properties . Clay Bricks are made of Silica, Alumina, Lime, Iron, Manganese, Sulfur, and Phosphates. They are poor conductors and are non combustible.

seven
Télécharger la présentation

Brick Manufacture

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Brick Manufacture Carlos Brown, Corey Henriquez, Michael Berry, R.J. Lavigne The Knack 11/30/10

  2. Basic Brick Properties • Clay Bricks are made of Silica, Alumina, Lime, Iron, Manganese, Sulfur, and Phosphates. They are poor conductors and are non combustible. • Young’s modulus = 1.5 x 106 psi – 5.0 x 106 psi • Modulus of Rupture = 500 – 3800 psi • Density = 125 pcf • Common uses include building, facing, flooring, and paving.

  3. Manufacture Process Overview

  4. Mining and Storage • 3 Types of Clay are used to make Brick • Surface Clays – sedimentary formations found on the surface • Shales – clays subject to high pressures until nearly hardened into slate • Fire Clays – mined at deeper levels than other clays • Mined in open pits then transported to plant storage areas

  5. Manufacture Process Overview

  6. Size Reduction • Dry Pan Crushers- Breaks large chunks of clay or shale • Grinders- pulverizes the clay to a fine consistency (Muller Wheels) • Important to have clays dry when grinding

  7. Screening • Passes through Vibrating Screen, Scalping Screen • Coarse material left goes back to grinder • Hammer mill • Large particles inhibit the durability of the brick

  8. Manufacture Process Overview

  9. Forming • Two steps in the forming process • Tempering • Water is added to the clay in a pug mill • Molding • Stiff Mud • Soft Mud • Dry-Press

  10. Manufacture Process Overview

  11. Drying • The moisture content of the formed clay is reduced, not eliminated, so that the brick will not explode during the firing process. • The clay is sent through a drying chamber for 24 to 48 hours at 100 to 400 deg F. • Heat and humidity must be regulated to avoid cracking in the brick

  12. Manufacture Process Overview

  13. Firing • Tunnel Kiln – Most Common, four stages • Final Drying and Dehydration: 300° F - 1800° F • Oxidation: 1000° F - 1800° F • Vitrification: 1600° F - 2400° F • Flashing: Varies depending on desired color

  14. Cooling and Processing • Tunnel Kiln-10 hours • Rate of Cooling has direct effect on color • Dehacking • Unloading a kiln after cooling • Bricks are sorted , graded, then packaged.

  15. Works Cited • Millberg, M. L. "How Brick Is Made - Material, Production Process, Manufacture, Making, Used, Processing, Dimensions, Industry, Raw Materials, The Manufacturing Process of Brick, Quality Control." How Products Are Made. How Products Are Made. Web. 29 Nov. 2010. <http://www.madehow.com/Volume-1/Brick.html>. • "Brick Manufacturing." Brickwork Design Guide by Glen-Gery Brick. Web. 29 Nov. 2010. http://www.glengerybrick.com/>. • "Manufacturing of Brick." Brick Industry Association - BIA. 2006. Web. 29 Nov. 2010. <http://www.gobrick.com/>.