Graphite Intercalation with Large Fluoroanions

Graphite Intercalation with Large Fluoroanions. Dept. of Chemistry and Center for Advanced Materials, Oregon State University. Intercalation. http://www.cem.msu.edu/~pinnweb/research-na.htm. Intercalation Hosts. Ion exchange: (fixed charge density)

thy
Télécharger la présentation

Graphite Intercalation with Large Fluoroanions

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Graphite Intercalation with Large Fluoroanions Dept. of Chemistry and Center for Advanced Materials, Oregon State University

  2. Intercalation http://www.cem.msu.edu/~pinnweb/research-na.htm Oregon State University

  3. Intercalation Hosts Ion exchange: (fixed charge density) smectite clay Nax+y[Al2-yMgySi4-xAlxO10(OH)2] layered double hydroxide [Mg3Al(OH)8]Cl metal phosphorous sulfide K0.4[Mn0.80.2PS3] Redox reaction: (variable charge density) metal dichalocogenide Lix[MoS2] layered oxides Lix[CoO2], Nax[MoO3] graphite K[C8], [C24]HF2 Oregon State University

  4. Energetics For clays – reaction is ion-exchange: Na+ Mont- + N(R)4+ Cl- (aqu) -> N(R)4+ Mont- + NaCl (aqu) For graphite – reaction is redox: Cx + A -> Cx+ A- ΔHrxn = I (Cx) - Ea (A) - ΔHL Oregon State University

  5. Graphite structure • C-C in-plane = 1.42 Å • Usually (AB)n hexgonal stacking • Interlayer distance = 3.354 Å Graphite is a semi-metal, chemically stable, light, strong A B Source: http://www.ccs.uky.edu/~ernst/ A Oregon State University

  6. + + + - - - Graphite Intercalation oxidant This is an acceptor-type GIC Donor-type reduces layers and intercalates cations Oregon State University

  7. GIC types ReductionM+Cx- Group 1 except Na Oxidation Cx+An- F, Br3-, O (OH) BF4-, P  BiF6- , GeF62- to PbF62-, MoF6-, NiF62-, TaF6-, Re  PtF6- SO4-, NO3-, ClO4-, IO3-, VO43-, CrO42- AlCl4-, GaCl4-,FeCl4-, ZrCl6-,TaCl6- Oregon State University

  8. Staging and dimensions Ic = di + (n - 1) (3.354 Å) For fluoro, oxometallates di≈ 8 A, for chlorometallates di≈ 9-10 A Oregon State University

  9. Graphite oxidation potentials H2O oxidation potential vs Hammett acidity Colored regions show the electrochemical potential for GIC stages. 49% hydrofluoric acid All GICs are unstable in ambient atmosphere , they oxidize H2O Oregon State University

  10. GIC special issues • Anions must be oxidatively stable • Larger anions could give larger galleries, wider range of chemistry • GICs that rapidly decompose in air or aqueous acid are hard to process further Oregon State University

  11. CxPFOS - preparation Cx+ K2Mn(IV)F6 + KSO3C8F17  CxSO3C8F17 + K3Mn(III)F6 (CxPFOS) Solvent = aqueous HF 3.35 A Oregon State University

  12. CxPFOS intercalate structure Anions self-assemble as bilayers within graphite galleries Oregon State University

  13. PFOS twist angle Chain twist defined by FC-CF tortion angle Oregon State University

  14. CxPFOS thermal stability CxPFOS KPFOS Oregon State University

  15. 1,2 Cx + K2MnF6 + LiN(SO2CF3)2 CxN(SO2CF3)2 + K2LiMnF6 oxidant anion source GIC O CF3 S N O O F3C S .. O New syntheses: chemical method 1. 48% hydrofluoric acid, ambient conditions 2. hexane, air dry Oxidant and anion source are separate and changeable. Surprising stability in 50% aqueous acid.

  16. CxN(SO2CF3)2 chem prepn Oregon State University

  17. F F F F New syntheses: N(SO2CF3)2 orientation

  18. CxN(SO2CF3)2 echem prepn 2  1 3  2 Oregon State University

  19. CxN(SO2CF3)2 - echem prepn CxPFOS CxN(SO2CF3)2 Oregon State University

  20. CxN(SO2CF3)2 anion orientation Oregon State University

  21. CxN(SO2CF3)2 thermal stability LiN(SO2CF3)2 Oregon State University

  22. Imide (NR2-) intercalates Anion MW di / Å N(SO2CF3)2 280 8.1 N(SO2C2F5)2380 8.2 N(SO2CF3) 430 8.3 (SO2C4F9) Oregon State University

  23. Other intercalated anions Anion MW di / Å C(SO2CF3)3 411 12.3 SO3C8F17 499 29.5 SO3C10F21 599 33.7 SO3C6F10(C2F5) 461 24.4 Oregon State University

  24. CxB(O2C2(CF3)4)2 Stage 1 1.13 0.85 nm 1.12 0.78 nm T Unexpected anion orientation - long axis to sheets Borate chelate GIC’s Blue: obs Pink: calc CxB(O2C2O(CF3)2)2 Stage 2

  25. Intercalation rates  Intercalate Temp / °C Reaction Anion  half-life / h SO3C8F17 20 10 N(SO2CF3)2 20 0.01 N(SO2CF3)(SO2C4F9) 70 100 N(SO2CF2CF3)2 70 500 C(SO2CF3)3 70 > 1000 SO3C6F5 20, 70 no reaction Oregon State University

  26. GIC ambient stabilities Oregon State University

  27. Application - IRP strategy 1. Intercalation 2. Removal 3. Optional cycle Targets • increase internal volume and disorder not surface area • low residual content Parameters: intercalate anion, reduction method (thermolysis, hydrolysis, hydrogenation) Oregon State University

  28. irrev reversible IRP charge-discharge • GIC is CxPFOS stage 2 • removal is by heating under N2 for 3 h • rate = C / 20 Oregon State University

  29. IRP for Li ion battery anodes e- + Cx + Li+ = CxLi Oregon State University