1 / 33

M1 Colloquium Presentation

M1 Colloquium Presentation. High Pressure Study of Na x TiNCl and CeFe 2. Arora Varun 29A13106 (Shimizu Lab). Contents. Introduction Motivation Experimental Method Results Summary. Intercalated MNX Compound ( Na x TiNCl ). Introduction. MNX

zola
Télécharger la présentation

M1 Colloquium Presentation

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. M1 Colloquium Presentation High Pressure Study of NaxTiNCl and CeFe2 AroraVarun 29A13106 (Shimizu Lab)

  2. Contents • Introduction • Motivation • Experimental Method • Results • Summary

  3. Intercalated MNX Compound(NaxTiNCl)

  4. Introduction • MNX M : Group IV metal ( Ti, Zr, Hf ) N : Nitrogen X : Halogen ( Cl, Br, I ) • Two types of layer-structured polymorphs of MNX ： • α-form(Orthorhombic ) • β-form ( Rhombohedra ) • Superconductivity uptoTc = 25.5 K in β-form :- • Lithium doped ZrNCl : Superconductivity at 13 K (1996) • Lithium doped HfNCl : Superconductivity at 25.5 K (1998) Superconducting Nitride Halides (MNX), Christian M. Schurz et al. , Zeitschrift for Kristallographie226, 395-416 (2011)

  5. TiNCl • α-MNX type structure • Layer Structure • [MN]+ layer is sandwiched between two sheets of halide anions [X]- • Orthorhombic Structure • Sensitive to moisture • Energy Band = 1.7 eV • (Semi-conductor) Cl N Basal Spacing Ti Superconducting Nitride Halides (MNX), Christian M. Schurz et al. , Zeitschrift for Kristallographie226, 395-416 (2011)

  6. What is Inter-calation? • To insert something between elements or layers. • Dopants can be introduced through the interlayer space without substituting or disturbing the original network for electron transport. • Two types of layer structured crystals : Molecular - Van der Walls force ( eg : Graphite ) Ion – exchangeable - Redox reaction ( eg : clay minerals ) Superconducting Nitride Halides (MNX), Christian M. Schurz et al. , Zeitschrift for Kristallographie226, 395-416 (2011)

  7. Previous Research on Na0.16TiNCl Superconducting Nitride Halides (MNX), Christian M. Schurz et al. Zeitschriftfor Kristallographie226, 395-416 (2011)

  8. Motivation On applying pressure, distance between the layers “d” decreases, and so Tcshould also increase ? Superconducting Nitride Halides (MNX), Christian M. Schurz et al. , Zeitschrift for Kristallographie226, 395-416 (2011)

  9. Check for Superconductivity in Na0.16TiNCl at High Pressure • Meisner Effect • Sharp change in • AC Susceptibility ( χ ) Resistivity Measurement • Sharp Drop in Resistivity Superconducting Nitride Halides (MNX), Christian M. Schurz et al. , Zeitschrift for Kristallographie226, 395-416 (2011)

  10. AC - Susceptibility Experiment

  11. AC Susceptibility and Superconductivity Bin = μ0nI = μ0M Bout = 0 If such a sample is placed in a external magnetic field, Ha, then Ba = μ0Ha Thus, Bin(total) = μ0(Ha + M) In case of paramagnetic material, in the absence of any external magnetic field, M = 0. M is directly proportional to the external magnetic field. Thus, M = χHa(χ : AC Susceptibility ) Thus, Bin(total) = μ0 (1+χ) Ha In Case of Superconductivity , Bin(total) = 0, therefore, χ = -1 Sample can be considered as a solenoid

  12. Principle of AC Susceptibility Measurement B (Magnetic field by primary coil) : Kept small, on the order of few Oe, so as not to avoid local heating f (Frequency of the field) : Increasing frequency increases not only the signal size but also the noise. n, r (No. of turns , radius of pick up coil) : Signal size is directly proportional to number of turns and radius of coil, but there is a limitation to both of these parameter when we are dealing with high pressure experiment. Vs, Vc(Volume of sample and coil) : Increasing the ratio of Vs/Vc will make the signal stronger

  13. Setting(AC Susceptibility Measurement) • Primary Coil • Cu wire (diameter = 100 μm) • Number of turns = 350 • Pick up Coil • Cu wire (diameter = 16 μm) • Diameter of coil = 300 μm

  14. Results

  15. Setting 1 Pressure Medium : Fluorinert 70 + 77 (1:1) Sample : Na0.16TiNCl and Pb Pressure : 0.1GPa Fluctuations due to change in the heater range! Pb

  16. Setting 2 Pressure Medium : Fluorinert 70 + 77 (1:1) Sample : Na0.16TiNCl and Pb Pressure : 0.1GPa Pb

  17. Setting 3 ( No pressure medium ) Sample : Na0.16TiNCl and Pb Pressure : 0.1GPa Pb

  18. Pb Pb Heating (0.5V) Heating (1V)

  19. Resistivity Measurement( 4‐probe Method)

  20. Ruby Sample • 1GPa • 1.5 GPa Gasket Insulating Layer 500 mm

  21. Summary • Na0.16TiNCl shows superconductivity at Tc= 18.1 K at ambient pressure. • Exact reason for no superconductivity observed when pressure is applied is not known, but possible reasons which can be given are : • Sample is sensitive to air/moisture, so there is a chance that sample was contaminated while installing it between the diamonds. • Maybe on applying pressure, it undergoes some structural change, and Na0.16TiNCl does not show superconductivity.

  22. Next Plan • Try to load sample inside the cell with even more care, so that is there is absolutely no contamination with air/moisture. • Next time see the crystal structure of Na0.16TiNCl under pressure and see if there is any change in structure.

  23. CeFe2

  24. n(r) r/rB Introduction Pm La Ce Pr Nd Sm Eu Gd Tb Dy Ho Tm Yb Lu ・Lanthanide 1s2 2s2 2p6 3s2 3p6 3d10 4s2 4p6 4d104f 1 5s2 5p6 5d1 6s2 Ce Localized or delocalized Ce • Cubic C15 Laves Structure (MgCu2) • Strongly hybridized compound between Fe 3d electrons and Ce 4f electrons. Fe

  25. CeFe2 v/s other REFe2 compounds • CeFe2 has lower Tc (around 230K) than other REFe2 compounds(around 600K). • The ferromagnetic ordering temperature is higher in the REFe2 compounds because of strong Fe-Fe interaction. • In case of CeFe2 , the Fe3d - Fe3d interactions compete with Fe3d - Ce4f interactions, and thus has lower Tc. Temperature Dependence of the Electrical Resistivity of REFe2, Gratzet al. , Solid State Communication, Vol.69,No. 10 (2011)

  26. Competing Ferro-Antiferromagnetic interaction in CeFe2 Ferromagnetism in CeFe2 is unstable because of competition between Fe3d- Fe3d interaction (Ferromagnetic) and Fe3d - Ce4f interaction (Anti-ferromagnetic). Presence of such a delicate balance between Ferromagnetism and Anti-ferromagnetism in CeFe2 has been proved by two methods : Doping CeFe2 with Co or Al High Pressure Antiferromagnetic order in pure CeFe2 under pressure, Braithwaite et al, Phys Rev B 76 (2007)

  27. Previous Research(High Pressure) On applying pressure, distance between Ce and Fe decreases 3d - 4f interactions increases Anti-ferromagnetic becomes prominent Antiferromagnetic order in pure CeFe2 under pressure, Braithwaite et al, Phys Rev B 76 (2007)

  28. Motivation To know how this system behave under pressure when the 4f-3d hybridization is enhanced in CeFe2

  29. Experiment Setting Gasket 100 mm

  30. My Results Tc ( My Experiment ) Tc @ 0.25 GPa

  31. Summary • CeFe2 is a strongly hybridized in which Anti-ferromagnetic state is unstable. • Anti-ferromagnetic stability can be achieved by applying pressure or by doping pure CeFe2 with Co or Al

  32. Next Plan Apply higher pressure and study the effect of increased 3d-4f interactions in CeFe2