CONFOCAL SPECTROMICROSCOPY OF AMORPHOUS AND NANOCRYSTALLINE TUNGSTEN OXIDE FILMS

CONFOCAL SPECTROMICROSCOPY OF AMORPHOUS AND NANOCRYSTALLINE TUNGSTEN OXIDE FILMS A. Kuzmin , R. Kalendarev, A. Kursitis, J. Purans E-mail: a.kuzmin@cfi.lu.lv. NCM-10, Praha (Czech Republic), September 18-22, 2006 . State-of-the-Art.

donny
Télécharger la présentation

CONFOCAL SPECTROMICROSCOPY OF AMORPHOUS AND NANOCRYSTALLINE TUNGSTEN OXIDE FILMS

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. CONFOCAL SPECTROMICROSCOPY OF AMORPHOUS AND NANOCRYSTALLINE TUNGSTEN OXIDE FILMS A. Kuzmin, R. Kalendarev, A. Kursitis, J. Purans E-mail: a.kuzmin@cfi.lu.lv NCM-10, Praha (Czech Republic), September 18-22, 2006.

  2. State-of-the-Art • “Blu-ray” disks, having capacity of more than 25 GB per recording layer,use a 405 nm laser, focussed through a high numerical aperture (NA=0.8-1.0) objective lens to a spot size of about 300 nm. • The most frequently used rewritable phase change recording materials, belong to the group of semiconductor chalcogenides. • For example: ternary GeSbTe and quaternary AgInSbTe alloys. • Other materials - tungsten oxides: - a reversible photoredox reaction under two-wavelength laser excitation of tungsten oxide in air • J.M. Osman, R.J. Bussjager, F. Nash, J. Chaiken, R.M. Villarica, Appl. Phys. A 66 (1998) 223. • - heat treatment of WO3/metal thin-film bilayered structures • Y. Takeda, N. Kato, T. Fukano, A. Takeichi, T. Motohiro, S. Kawai, J. Appl. Phys. 96 (2004) 2417. • - rewritable electrically selective multi-layered optical recording disk, based on the electrochromic behaviour of WO3 • R. Sato, N. Ishii, N. Kawamura, H. Tokumaru, in: Proc. 3rd European Symp. • on Phase Change and Ovonic Sci., Balzers, Liechtenstein, September 04-07, 2004. • - write-once optical recording was demonstrated in WO2 film • T. Aoki, T. Matsushita, A. Suzuki, K. Tanabe, M. Okuda, Thin Solid Films 509 (2006) 107.

  3. Present work goal • To demonstrate the possible use of WO3 & AWO4 thin films for write-once phase change optical recording. • To propose the multilayer AWO4 phase-change media structure based on Raman scattering detection of the highest frequency stretching W-O mode.

  4. 3D scanning confocal microscope with spectrometer "Nanofinder-S" produced by SOLAR TII, Ltd. • Simultaneous / Multifunctional Analysis: • Optical and Confocal Microscopy • Raman Spectroscopy • Luminescence Spectroscopy • 0D, 1D, 2D & 3D High-speed Imaging and Spectroscopy

  5. "Nanofinder-S" modular optical layout He-Cd 441.6 nm 50 mW

  6. Commercial Compact Disk Imaging in Confocal Mode CD-ROM CD-R CD-RW Track pitch = 1.6 µm Track pitch = 1.6 µm Track pitch = 1.6 µm Images size: 2024 µm

  7. N S S N Thin Film Preparation by DC Magnetron co-Sputtering Metallic targets: W (99.95%) Ni (99.0%) Zn (99.9%) Substrates: Si, glass Sputter gas: Ar (80%) + O2 (20%) Total gas pressure: 6.7 Pa Discharge power: 100 W Sputter Gas SUBSTRATE Plasma Glow Metallic Target / Cathode Magnets

  8. W O Crystalline Structure of WO3 WO3: [WO6] Well known electrochromic material based on valence change of tungsten ions: W6+ (transparent)  W5+ (blue)

  9. Crystalline Structure of AWO4 (A = Ni, Zn ) A W O AWO4: [AO6] & [WO6] Tungstates are known as scintillators and Raman shifters.

  10. * A. Kuzmin, J. Purans, E. Cazzanelli, C. Vinegoni, G. Mariotto, J. Appl. Phys. 84 (1998) 5515. a-W6+O3 W(6-y)+ c-W6+O3 Optical Recording in t.f.-WO3 Confocal images: 274 m × 333 m 15 mW 25 mW 50 mW O-W-O stretching modes O-W-O & W=O stretching modes

  11. O-W-O stretching modes Optical Recording in t.f.-NiWO4 25 mW 50 mW 15 mW Confocal images: 134 m × 167 m 700°C * A. Kuzmin, J. Purans, R. Kalendarev, D. Pailharey, Y. Mathey, Electrochim. Acta 46 (2001) 2233.

  12. Optical Recording in t.f.-ZnWO4 O-W-O stretching modes 700°C W-O-W bending modes 50 mW

  13. W6+O3-x & AW6+O4-x (A = Ni, Zn) • Formation of metastable color centers W6+ W(6-y)+ • short term life time in air • Crystallization to WO3 / AWO4 • long term life time • good thermal stability Change in reflectivity (10-20%) Change in phase & reflectivity Multilayer phase-change media structure based on Raman scattering detection Possible Mechanismsof Optical Recording in Tungsten Oxides

  14. Raman signal 1 1,..., n Dielectric layer Dielectric layer Phase-change A1WO4-x layer Phase-change A1WO4-x layer Dielectric layer Dielectric layer ... ... n-layers n-layers Phase-change AnWO4-x layer Phase-change AnWO4-x layer Dielectric layer Dielectric layer Metallic mirror layer Metallic mirror layer Substrate Substrate Sequential Writing Parallel Reading Multilayer write-oncephase-change media structure based on Raman scattering detection AWO4 band gap ~ 3.0-3.8 eV

  15. Thank you ! For more information look at the Internet: http://www.cfi.lu.lv/exafs This work was supported by the Latvian Government Research Grants and National Research Program in Materials Science.