1 / 8

Reconstruction of the Surface of GaAs Film

MatSE390 Project. Reconstruction of the Surface of GaAs Film. Yunfeng Shi. FLUX RATIO. RHEED,SEM. FILM GROWTH. TEMPERATURE. Introduction.

alma
Télécharger la présentation

Reconstruction of the Surface of GaAs Film

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. MatSE390 Project Reconstruction of the Surface of GaAs Film Yunfeng Shi

  2. FLUX RATIO RHEED,SEM FILM GROWTH TEMPERATURE Introduction Thin-film growth on a GaAs(001) surface, either homoepitaxial or heteroepitaxial, has a great technological importance when developing optoelectronic devices. In order to get high quality of film, we must control the surface reconstruction. This is called surface-structure-controlled epitaxy. Feed Back

  3. Algorithm Monte Carlo Method and Metropolis Algorithm are used here. The top-most layer is our interest. Since in experiments, there will be two types of surface, Ga-rich surface and As-rich surface, while they have different characteristics. The first few layers near surface are also allowed to move. Lattice Model is also used to fast the speed. A modified Tersoff Potential is used:

  4. Results From normal Monte Carlo method, we can find that As-rich acts quite differently compared to Ga-rich surface. Ga atoms are much more active than As atom. We can see from below:At 3000k, After 60000 runs, As atoms mostly stay at the original position, while Ga atoms moves a lot.

  5. Single As atom Potential Contour Single Ga atom Potential Contour

  6. POTENTIAL CURVES

  7. Starting postition Final position Analysis: 9/25 type RECONSTRUCTION OF GA-RICH SURFACE

  8. Conclusion Surface reconstruction can be got by Monte Carlo method for the GaAs film. It can be faster if using lattice model. We can also see the different behaviors of Ga and As atoms on surface.