Chapter 7 High temperature deformation of crystalline materials-2

Chapter 7 High temperature deformation of crystalline materials-2. Primary creep, Stage I, is a period of decreasing creep rate. Primary creep is a period of primarily transient creep. During this period deformation takes place and the resistance to creep increases until stage II.

daquan-neal
Télécharger la présentation

Chapter 7 High temperature deformation of crystalline materials-2

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Chapter 7 High temperature deformation of crystalline materials-2

  2. Primary creep, Stage I, is a period of decreasing creep rate. Primary creep is a period of primarily transient creep. During this period deformation takes place and the resistance to creep increases until stage II. Secondary creep, Stage II, is a period of roughly constant creep rate. Stage II is referred to as steady state creep. Tertiary creep, Stage III, occurs when there is a reduction in cross sectional area due to necking or effective reduction in area due to internal void formation. The following stages are observed: 1. The incubation deformation. 2. The primary stage. The creep rate decreases when the strain increases. 3. The steady-state strain. The plastic strain rate is a constant value. ε˙ = const. 4. The tertiary stage. The tertiary creep leads to a rupture.

  3. http://engineering.dartmouth.edu/defmech/

  4. Low-temperature plasticity limited by a lattice resistance. The strain-rate is determined by the kinetics of kink nucleation and propagation. Low-temperature plasticity limited by discrete obstacles. The strain-rate is determined by the kinetics of obstacle cutting.

  5. Diffusional flow by diffusional transport through and round the grains. The strain-rate may be limited by the rate of diffusion or by that of an interface reaction.

  6. Power-law creep involving cell-formation by climb. Power-law creep limited by glide processes alone is also possible.