An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Superconductivity in MgB2 Khalil Ziq Physics Department KFUPM April 12 2003

  2. New Superconductor Developments -Fullerenes: Tc engineered to 117K. -Iron and Sulfur become SC under pressure. -Plastic SC: polythiophene. -DNA can be made superconducting. -MgB2 changes our thinking (again).

  3. The Borides WorldMgB2 Jan 10 2001Jun AkimitsuAPS March 2001 Ferromagnetism: EuB6 with S=7/2 4f-electron local moment and TC=16 K Ca1-xLaxB6 with 0.1 mB/La and TC=600-1000 K CaB2C2 with 0.0001 mB /f.u. and TC=770 K Superconductivity: LNi2B2C with L=Lu, Tm, Er, Ho, Dy, Y) and Tc=6-17 K MgB2 with Tc=39 K Boron: From the Arabic Buraq. Magnesium: District of Magnesia Greece,

  4. MgB2

  5. MgB2 Production • Mg : B = 1:2 molar ratio Ground mixture for 15 minutes Pressed into 1g pellets • Heat @800-950 C for 2hours.

  6. Structure The boron atoms form graphite-like sheets separated by hexagonal layers of Mg atoms.

  7. Equilibrium Magnetization

  8. M=-Moln(Hc2/H)Mo~λ^2 Evaluate Hc2, Hc and Mo

  9. Helfand-Werthamer Welp et al. Sologubenko et al. Angst et al. Upper Critical Field Hc2 Along the c-Axis Ziq Perucchi et al., Phys. Rev. Lett. 89, 097001 (2002)

  10. Scaling of Meq

  11. Hysteresis loops

  12. Pinning force=H*Jc

  13. Max. Pinning Force

  14. Conclusion • Thermodynamic results supports clean limit SC, unlike optical results which support a dirty-limit scenario • The superconducting gap with 2D/kBTc~1.2 is substantially below the estimate of the weak-coupling BCS theory. • The optical conductivity rises in an s-wave like manner.