Secondary Electron Detection

Secondary Electron Detection. CAMTECH 2011 Regi. INTRO. High energy e - beam scans sample surface ( Raster - line by line). Provides information about surface and near-surface atoms – topography and chemical composition. Stereoscopic images (3D perspective). BEAM-SAMPLE INTERACTIONS.

giulio
Télécharger la présentation

Secondary Electron Detection

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Secondary Electron Detection CAMTECH 2011 Regi

  2. INTRO • High energy e- beam scans sample surface (Raster - line by line). • Provides information about surface and near-surface atoms – topography and chemical composition. • Stereoscopic images (3D perspective)

  3. BEAM-SAMPLE INTERACTIONS Incident beam BSE Emissions of SE Electrostatic force 10nm Constituent atoms

  4. BEAM-SAMPLE INTERACTIONS • Backscattered Electrons (BSE) increase in reflectivity with growth in atomic number • Secondary electrons (SE) predominantly produced by the interactions between highly energetic beam electrons and weakly bonded. • Only SE produced within a depth of 10 nm can escape the sample

  5. Secondary Electrons • Energy below 50 eV • Electron Emission Yield • The bigger the yield the bigger the signal intensity - varies from material to material - increases with e--beam incident angle SE BSE Relative count of emitted e- 1 10 100 1k 10k 20k Energy of e- emitted from specimen (log eV)

  6. SE Images • Carry information about topography and defects adjacent to surface (depth) – 10 nm BSE SE

  7. SE Detection • Distinguished SE1, SE2 and SE3 SE1: emitted from the e--beam irradiation point SE2: emitted along with the springing-out process of BSE SE3: due to BSE collisions with Parts other than the specimen

  8. SE Detection Everhart and Thornley Detector: designed in 1960 to collect and amplify the signal provenient from SE Dynode Collecting electrode Scintillator SE Light guide Photoelectric conversion face

  9. Thanks!