Tool Steel – Knife Making. Presented by: Noah Nordhoff Joseph Easterbrook. ENGR 45 Fall Semester 2010 Dr. Younes Yataiiyan. Choosing the right steel:. Ability to harden, anneal and work Specific Properties High Carbon (.35%+) Tool – 1095 (Ka-Bar) Stainless 440 (A B C) Alloy.

ince
Télécharger la présentation

Tool Steel – Knife Making

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Tool Steel – Knife Making Presented by: Noah Nordhoff Joseph Easterbrook ENGR 45 Fall Semester 2010 Dr. Younes Yataiiyan

  2. Choosing the right steel: • Ability to harden, anneal and work • Specific Properties • High Carbon (.35%+) • Tool – 1095 (Ka-Bar) • Stainless • 440 (A B C) • Alloy

  3. Preliminary metal tests: High Carbon (see dark carbide area)  Large File - pre-anneal Low Carbon- Alloy? (see light ferrite area) Small File – post-anneal 

  4. From file to flat stock: • Anneal & test softness • Kiln – Cone 4 (over 2100 deg. F) • http://www.claymentality.net/index.php?pagekey=conechart • Remove Ferrous Oxide • Sand to remove more burrs – desired finish

  5. Remove Ferrous Oxide and test softness

  6. Shaping the blade • Rough out design • Sketch on blank • Cut off extra material • Grind • Rough out shape • Thin desired sections • Start to form the blade • File • Smooth ground sections/ define blade structure

  7. Grind & File Safety First! 

  8. Quenching • Need to add hardness • Use blow torch to heat blade • Quench in water • Alternate: Wrap blade in clay except for sharp edge, then place in kiln at ~2000 deg F and quench http://evergreen-rentals.com/index.php?main_page=index&cPath=2_40

  9. Form Handle • Create “pommel” or finger guard • Create shoulder at end to prevent hand from slipping • Will later cover in wood and rivet or epoxy in place

  10. Conclusion • Absolutely have to use hard metal such as high carbon steel, stainless steel, titanium alloy, etc. • Must anneal high carbon steel • Form steel to desired shape • Harden blade for long lasting sharpness

  11. Acknowledgment Many thanks to my sister Ruth and her boss for letting us use the Kiln, also to my Dad and brother for the files and tips for grinding.

  12. Questions?