1 / 16

Muntz Metal

Muntz Metal. An Analysis of Muntz Metal’s properties and its Application as a Building Material. Muntz Metal= 60% copper + 40% Zinc + small amount of iron.

luna
Télécharger la présentation

Muntz Metal

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Muntz Metal An Analysis of Muntz Metal’s properties and its Application as a Building Material

  2. Muntz Metal= 60% copper + 40% Zinc + small amount of iron • The purpose of adding alloying elements to copper is to optimize the strength, ductility (formability), and thermal stability, without inducing unacceptable loss in fabric ability, electrical/thermal conductivity, or corrosion resistance. • The existence of impurities and all common alloying elements, except for silver, will decrease the electrical and thermal conductivity of copper.)

  3. Mechanical Properties

  4. Hardness Indentation hardness measures the resistance of a sample to permanent plastic deformation due to a constant compression load from a sharp object • Rockwell F: 1/16 inch Braleindenter60 kg load • >> The hardness value is above the acceptable range of the particular hardness scale.

  5. Sheer Strength • The shear modulus is concerned with the deformation of a solid when it experiences a force parallel to one of its surfaces while its opposite face experiences an opposing force (such as friction). • It is defined as "the ratio of shear stress to the displacement per unit sample length (shear strain)" .

  6. Shear Modulus • Shear Modulus is the coefficient of elasticity for a shearing force. It is defined as "the ratio of shear stress to the displacement per unit sample length (shear strain)" • the shear modulus describes the material's response to shearing strains. • It is the description of an object’s tendency to be deformed elastically.

  7. Thermal Conductivity (in/hr*ft²*°F)

  8. Thermal Expansion (in²/°F x 10^-6)

  9. Specific Heat Capacity

  10. Corrosion Resistance • Copper corrodes at negligible rates in unpolluted air, water, and desecrated non-oxidizing acids. Copper alloy artifacts have been found in nearly pristine condition after having been buried in the earth for thousands of years, and copper roofing in rural atmospheres has been found to corrode at rates of less than 0.4 mm in 200 years. • Copper alloys resist many saline solutions, alkaline solutions, and organic chemicals. However, copper is susceptible to more rapid attack in oxidizing acids, oxidizing heavy-metal salts, sulfur, ammonia (NH3), and some sulfur and NH3 compounds • Brasses (C 20500 - C 28580) are basically copper-zinc alloys and are the most widely used group of copper alloys. The resistance of brasses to corrosion by aqueous solutions does not change markedly as long as the zinc content does not exceed about 15%. Above 15% Zn, dezincification may occur.

  11. Dezincification • Dezincification results in a porous, reduced ductility, reddish copper matrix. What remains may support a given load until an increase of pressure or weight exceeds the local ductility and causes fracture. Soft, stagnant, or slow moving waters or saline solutions can lead to dezincification of unmodified brasses. The brasses may be more prone to dezincification in stressed regions (for example, in the bent region of a float arm on a water closet fixture) or where a bend exists (as in an elbow in a fresh water supply line). • High zinc content introduces the possibility of stress-corrosion cracking. Very high zinc content, as in Muntz metal, may lead to excessive corrosion attack in seawater due to dezincification. • (Limited or no data are available on the effects of zinc in brasses on the rate of corrosion; however, the addition of tertiary and quaternary elements is known to enhance the resistance of zinc-containing alloys to certain environments.)

  12. Stress corrosion cracking (SCC) • Stress Corrosion Cracking is cracking due to the process involving conjoint corrosion and straining of a metal due to residual or applied stresses SCC is the growth of cracks in a corrosive environment. It can lead to unexpected sudden failure of normally ductile metals subjected to a tensile stress, especially at elevated temperature in the case of metals.

  13. The SCC environment of Muntz • Alloys at the higher zinc levels of 35 to 40% Zn contain the bcc beta phase, especially at elevated temperatures, making them hot extrudeable and forgeable. • When subjected to the combined effects of stress and corrosion, many alloys can develop cracks over a period of time and specifically copper-zinc alloys such as brass can be sensitive to stress corrosion attack, particularly in the presence of moisture through condensation. However, SCC occurs only in the presence of a sufficiently high tensile stress and a specific corrosive environment. For brasses, the environment involved is usually one containing ammonia or closely related substances such as amines.