Elongation Requirements for Stainless Steel Rebar Presented by: Suresh Gupta

Elongation Requirements for Stainless Steel Rebar Presented by: Suresh Gupta ASTM Committee Meeting A01.05 May 8, 2012. Purpose of Elongation .

shiloh
Télécharger la présentation

Elongation Requirements for Stainless Steel Rebar Presented by: Suresh Gupta

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Elongation RequirementsforStainless Steel Rebar Presented by: Suresh Gupta ASTM Committee Meeting A01.05 May 8, 2012

  2. Purpose of Elongation • Elongation is a measure of ductility, which provides confidence that metals can be formed, without cracking or fracturing. • In rebar, it defines ductility so that bars can be bent without cracking. • If bars do not crack during fabrication, any excess elongation is irrelevant.

  3. Alloy Characteristics With all other variables remaining same, • Austenitic Alloys have highest elongation. • Duplex Alloys have elongation in mid range • Ferritic Alloys have lowest elongation

  4. Measurement Methods and Facts • % Elongation, when measured in a fixed gage length, e.g. 8 inches, is lower than when measured in a gage length, as a multiple of diameter, e.g. 4 X diameter (4d). (when 4d is less than fixed gage length). • Elongation is generally lower as diameter goes smaller. • This fact is clearly described in ASTM E8, Appendix XI

  5. ASTM E8Standard Test Method for Tension Testing of Metallic MaterialsAppendix XI – Factors Affecting Tensile Test Results • Comparison of elongation values determined using different specimens requires that the following ratio be controlled: Lo/(Ao)1/2 (XI.1) Where: Lo = original gage length of specimen, and Ao= original cross-sectional area of specimen. XI.4.4.1 Specimens with smaller Lo/(Ao)1/2 ratios generally give greater elongation. Note: (Ao)1/2 is proportional to diameter (d). Therefore, for same ductility, larger diameter samples result in greater elongation values, when measured in fixed gage length.

  6. ASTM A955-9a • Until revision 10a, elongation was not required for • sizes # 3-5 Grade 75, probablybecause it was known that it is unrealistic or not necessary. • Grade 40 for sizes 7 and larger because, in any condition it will meet the requirement, anyway.

  7. % Elongation Requirements for Rebar Carbon and Alloy steels • ASTM A615 requires 6 to 7% for Grade 75 • ASTM A706 requires 10 to 14% for all Grades. Stainless Steels • BS 6744 requires 14% minimum in 5d gage length for Grade 500 (72.5 ksi). • ASTM A955 requires 20% minimum in 8 inch gage length for all grades, all sizes.

  8. Manufacturing & Process Control • Even with precise chemistry and process control, duplex stainless steels meet the elongation requirement very marginally. • If rebar is supplied in coils, machine straightening will cause work hardening and elongation will go down even further. • This may cause unnecessary dispute.

  9. Rationale • If 6% elongation in carbon steel is sufficient • If 14% in 5d is sufficient for stainless steel rebar per BS6744 in Europe, • It should be sufficient for us as well. FYI • ASTM Specifications for plain smooth bars require elongation in 4d

  10. Proposal • It is therefore recommended that, • Using a foot note to Table 3, elongation requirements be lowered to 14% for Grade 75, • for all sizes of duplex grades and, • all grades of stainless steels under 1.00 inch.