1 / 1

The Morphology of Laser-Synthesized Carbon Nano-Fillers: the Influence on Polymer-Based Composites

The Morphology of Laser-Synthesized Carbon Nano-Fillers: the Influence on Polymer-Based Composites. Lavinia Gavrila-Florescu 1* , Ion Sandu 1 1 National Institute for Lasers, Plasma and Radiation Physics, P.O. Box MG-36, Bucharest, Romania

stasia
Télécharger la présentation

The Morphology of Laser-Synthesized Carbon Nano-Fillers: the Influence on Polymer-Based Composites

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. The Morphology of Laser-Synthesized Carbon Nano-Fillers: the Influence on Polymer-Based Composites Lavinia Gavrila-Florescu1*, Ion Sandu1 1National Institute for Lasers, Plasma and Radiation Physics, P.O. Box MG-36, Bucharest, Romania *IMT-Bucharest, 126A, Erou Iancu Nicolae street, 077190, PO-BOX 38-160, 023573, Bucharest, Romania MOTIVATION Carbon nanoparticles are considered high-potential filler materials for the improvement of mechanical and physical polymer properties; the focus of the work was to drive these materials into a regime where they can favorably interact with the matrix. GENERAL FEATURES OF CARBON NANOPOWDER SYNTHESIZED BY LASER-INDUCED PYROLYSIS • Coalescence in bigger particles. Agglomeration occurs already in the flame. • Bending through the graphite nano-ribbons • Size depends on gas composition and experimental parameters (10-60 nm) MAIN CARBON POWDER MORPHOLOGIES Fullerene-like (C6H6/C2H4/N2O) Carbon nano-ribbons (C2H2/SF6) C/F=3 TURBOSTRATIC (C2H2/SF6) TURBOSTRATIC (C6H6/C2H4) TESTS FOR POSSIBLE APPLICATIONS • Laser induced pyrolysis  morphologically different carbon nanopowders with specific chemical properties; Experimental confirmation by their particular behavior during interaction with different chemical and biological systems;  Electrical conduction of polymer/carbon composite strongly influenced by electrical resistivity of filler * sample’s density: 1.2 g/cm3 Ohmic behavior Resistivity vs carbon content 1/d002 and La vs (C/F)at ratio Resistance vs soot structure and morphology CONCLUSIONS  characteristics of the obtained nanocomposite are affected by properties and dispersion of the addition material;  the morphology of the carbon nanopowder depends on both gas mixture and experimental parameters;  optimal concentration of the filler was around 2% (wt);  better results obtained by addition of laser-synthesized carbon nanopowder;  the additional reinforcement with carbon/glass fibers led to an important enhancement of mechanic characteristics;  the studies are in progress. Acknowledgement: Some of the results were obtained in the frame of the Project POSDRU/89/1.5/S/63700.

More Related