Chris Chase EE235 4/9/07

Chris Chase EE235 4/9/07. Introduction. Nanowire Lasers Applications Potential solution for a laser integrated on silicon Nanowires act as a natural laser cavity Nanowire facets act as mirrors Nanowire itself guides light This makes a nanowire a natural Fabry-Perot Cavity.

walker-mitchell
Télécharger la présentation

Chris Chase EE235 4/9/07

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Chris Chase EE235 4/9/07

  2. Introduction • Nanowire Lasers • Applications • Potential solution for a laser integrated on silicon • Nanowires act as a natural laser cavity • Nanowire facets act as mirrors • Nanowire itself guides light • This makes a nanowire a natural Fabry-Perot Cavity

  3. Fabrication Process • Deposit Poly(9,9-dioctylfluorene) (PFO) on glass substrate • Place against porous alumina membrane • Anneal for 2 hrs at 250 C, where polymer melts into holes in membrane • Dissolve membrane in NaOH • Resulting nanowires are generally between 250 and 350 nm in diameter and on average 6 µm in length • Nanowires have a PL peak at ~460 nm, which is similar to the bulk PL.

  4. Material Characterization

  5. Waveguiding Scale bar is 5 µm Calculations show that ~85% of fundamental mode should be confined

  6. Cavity Characteristics

  7. Lasing Characteristics