1 / 11

Description of welding prototypes Results The new design - Conclusion

Description of welding prototypes Results The new design - Conclusion. Conical shape (welding length 14,79 mm). EB welding. Few welding points. 2 prototypes for the tests of EB welding. Goal : to see the deformations made by EB welding. (14,79 pm). 11. Ra 0,8. Steps :

bonner
Télécharger la présentation

Description of welding prototypes Results The new design - Conclusion

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Description of welding prototypes • Results • The new design • - Conclusion Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007

  2. Conical shape (welding length 14,79 mm) Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007

  3. EB welding Few welding points 2 prototypes for the tests of EB welding Goal : to see the deformations made by EB welding (14,79 pm) 11 Ra 0,8 • Steps : • manufacturing the parts A and B with coaxiality tolerances of 50 microns • to machine a centering device and to insert it inside A and B • make few welding points by EB welding • remove the centering device to avoid to keep it prisoner • make the EB welding 45°±10’ A B Ø 78 Ø 78 Ø 112 Ø 99 Ø 116 16 58 89 Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007

  4. 2 prototypes (14,79 pm) (14,79 pm) 11 11 Ra 0,8 Ra 0,8 45°±10’ 45°±10’ Ø 78 Ø 78 Ø 78 Ø 78 Ø 99 Ø 112 Ø 116 Ø 99 Ø 112 Ø 116 22 16 58 58 89 89 Short version Long version Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007

  5. 2 prototypes Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007

  6. RESULTS Parallelism : short version : 0,012 long version : 0,012 (14,79 pm) 11 Ra 0,8 45°±10’ Coaxiality : Short version : 0,114 Long version : 0,151 A B Ø 78 Ø 78 Ø 99 Ø 112 Ø 116 Misalignment : ≃ 50μ between A and B The welding stops up to 0,1mm from the inner side (welding depth of 14,69) 22 58 Leak tests : Short version : 1. 10-10mbar.l.s-1 Long version : 1. 10-10mbar.l.s-1 89 Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007

  7. RESULTS • To support the parts A and B during the EB welding • A large conical shape is not necessary (with a large conical shape, the welding power is higher therefore the deformation is also higher too) • The centering device must stay during the welding but must be demonstrable after the welding Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007

  8. Conical shape (length 4,85 mm) Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007

  9. Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007

  10. The proposal of the manufacturing process for the reentrant BPM Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007

  11. Conclusion • - a conical shape between the part A and the part B allows to centre , • on the other hand, a large support conical shape is not necessary and is perhaps unlucky (the large powerful introduces some deformations) • for reduce the deformations, the speed of welding must be increased, the depth of welding must be reduced Nelly Rouvière Cold BPM-XFEL Workshop 12-05-2007