1 / 20

NEG films: recent R&D progress Paolo Chiggiato (for the EST-SM-DA section)

Vacuum Issues of the LHCb Vertex Detector 28 November 2000. NEG films: recent R&D progress Paolo Chiggiato (for the EST-SM-DA section). Summary. - Higher substrate temperature during deposition - Clean gas venting - Other. - NEG films: choice and production - Pumping speed -Ageing.

breck
Télécharger la présentation

NEG films: recent R&D progress Paolo Chiggiato (for the EST-SM-DA section)

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Vacuum Issues of the LHCb Vertex Detector 28 November 2000 NEG films: recent R&D progressPaolo Chiggiato (for the EST-SM-DA section) Summary - Higher substrate temperature during deposition - Clean gas venting - Other... - NEG films: choice and production - Pumping speed -Ageing

  2. Choice of the NEG film materials High O solubility limit • The NEG film materials should allow a complete dissolution of the oxide layer at a reasonable low temperature: • High oxygen solubility limit • High oxygen diffusion coefficient • are needed. • If the activation process is limited only by diffusion the time needed to dissolve the oxide layer is: • ta ≈ D-1 (cs-co) -2 • Due to their low grain size, thin films have larger diffusivity and solubility than the respective bulk, therefore faster dissolution

  3. Choice of the deposition technique • Composite cathodes • allow the production of compounds/alloys starting from easily available pure metals • eliminate the problem of cathode pyrophoricity • Sputtering is the ideal production technique because: • simple and suitable for a wide range of materials • keeps stoichiometry of alloys • suitable for distributed coating • allows co-sputtering from composite cathode • allows the production of materials far • from thermodynamic equilibrium

  4. Ti-Zr-V The composition of coatings produced from a cathode made of three inter-twisted wires of the same diameter of Ti, Zr and V is 30-30-40 [at.%]. The onset of the activation process is between 150°C and 200°C (2h).

  5. TiZrV/St.St. Influence of the substrate material (I) TiZrV/Cu Ti-Zr-V films deposited on copper and stainless steel have a very smooth surface, whereas those deposited on aluminium and beryllium have a granular structure. 1 µm TiZrV/Al

  6. Influence of the substrate material (II) Spreading of the ESD results obtained for Ti-Zr-V films deposited on stainless steel, Al-6062 and copper Ultimate pressure achieved in Ti-Zr-V coated stainless steel and Al chambers, L = 2 m, Ø = 10 cm, applied pumping speed = 25 l s-1 for H2

  7. Pumping speed of Ti-Zr-V coatings: heating temperature Pumping speed of a Ti-Zr-V thin film deposited on Al-6062 strips.

  8. Pumping speed of Ti-Zr-V coatings: heating time

  9. S=S(Q)

  10. Ageing (Ti-Zr-V on St. Steel)

  11. Ageing (Ti-Zr-V on Aluminium)

  12. Influence of the temperature of the sample during deposition The standard temperature of the substrate during deposition is 100 °C, but substrate temperatures ranging from liquid N2 to 400 °C (for Al up to 200°) are applicable. Ti-Zr-V films were deposited on Cu and stainless steel at 300°C: the results are promising. Ti-Zr-V films deposited on Al, Cu and stainless steel at 200°C will be prepared soon and the results will be available before the end of the year.

  13. Temperature of the substrate at 300°C during deposition (I)

  14. Temperature of the substrate at 300°C during deposition (II)

  15. Temperature of the substrate at 300°C during deposition (III)

  16. Temperature of the substrate at 300°C during deposition (IV)

  17. Microstructure of a Ti-Zr-V film deposited at 300°C

  18. Clean Gas Injection

  19. Clean Gas Injection

  20. Conclusions • Many getter coatings were produced which undergo activation when heated at temperatures lower than 400°C. The lowest activation temperature (180°C for 24 h heating) has been recorded for Ti-Zr-V films deposited from a cathode made of three inter-twisted elemental wires. • Ti-Zr-V films deposited on Al. Cu, Be and stainless steel have similar vacuum behaviour even if their microstructure can significantly differ. • Sticking probability of about 10-2 for H2 and 5x10-1 for CO can be obtained with Ti-Zr-V films. The saturation of the surface is obtained after pumping of 5 to 7 x 1014 CO molecules cm-2. • Ti-Zr-V films deposited on Cu or stainless steel at 300°C have shown: # higher pumping speeds for the lowest heating temperatures # larger saturation value than those deposited at the standard temperature (100°C).