Laser Heating On the Surface of Au(111) covered with Octanethiol

Laser Heating On the Surface of Au(111) covered with Octanethiol. By: Chris Agostino. Unannealed Gold. 50 nm range This was a test of the laser and other functions. Before: 7-1-11AP, 5 minutes exposed to laser After: 7-1-11AQ, 5 minutes cooling. Annealed Gold. 50 nm range

dalton
Télécharger la présentation

Laser Heating On the Surface of Au(111) covered with Octanethiol

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Laser Heating On the Surface of Au(111) covered with Octanethiol By: Chris Agostino

  2. Unannealed Gold • 50 nm range • This was a test of the laser and other functions. • Before: 7-1-11AP, 5 minutes exposed to laser • After: 7-1-11AQ, 5 minutes cooling

  3. Annealed Gold • 50 nm range • This was another day of scanning for testing purposes. • Before: 7-5-11AK, 5 minutes exposed to laser • After:7-5-11AL, 5 minutes cooling

  4. Au(111) with DTC2 and Octanethiol • 67.2 nm range • Before: 7-7-11AE, 6 minutes exposed to laser • After:7-7-11AF, 6 minutes cooling

  5. Au(111) with DTC2 and Octanethiol • 67.2 Scan Range • Before:7-7-11AG, 5 minutes exposed to laser • After: 7-7-11AH, 5 minutes cooling

  6. Au(111) with DTC2 and Octanethiol • 200 nm range • Before: 7-7-11AI, 7 minutes exposed to laser • After: 7-1-11AJ, 7 minutes cooling

  7. Au(111) with Octanethiol • 50 nm range • Before: 7-18-11AD, 30 seconds exposed to laser • After: 7-18-11AE, 30 seconds cooling

  8. Au(111) with Octanethiol • 26.2 nm Range • Before: 7-21-11AQ, 45 seconds exposed to laser • After:7-21-11AR, 45 seconds cooling

  9. Au(111) with Octanethiol • 50 nm Range • Before: 7-22-11AC, 45 seconds exposed • After: 7-22-11AD, 45 seconds cooling

  10. Au(111) on Octanethiol • 37.3 nm Range • Before: 7-22-11AH, 35 seconds exposed to laser • After: 7-22-11AI, 70 seconds cooling

  11. Au(111) with Octtanethiol • 38.9 nm Range • Before: 7-26-11AE, 35 seconds exposed to laser • After: 7-26-11AF, 70 seconds cooling

  12. Au(111) on Octanethiol • 25 nm Range • Before: 090811AE, 45 seconds exposed to laser • After: 090811AF, 90 seconds cooling • +.5V, 1.001 C, P=7, I=7, Res: 256;256

  13. Au(111) on Octanethiol • 60.2 nm Range • Before: 090811AG, 45 seconds exposed to laser • After: 090811AH, 90 seconds cooling • +.5 V, 1.001 C, P=7, I=7, Res: 512;256

  14. Au(111) with Octanethiol • 84.8 nm range • Before: 092211AF, 50 seconds exposed to laser • After:092211AG, 2 minutes cooling • +.5 V, 1.001 C, P=7, I=7m Res: 512;512

  15. Au(111) with Octanethiol • 62.5 nm Range • Before: 092911AB, 50 seconds exposed to laser • After: 092911AC, 5 minutes cooling • +.5 V, 1.001 C, I=7, P=7, Res:256;256

  16. Au(111) with Octanethiol • 50.8 nm Range • Before: 100511AB, exposed to laser for one minute • After: 100511AC, cooling for five minutes • +.5 V, 1.001 C, P=10, I=10, Res: 256;256

  17. Au(111) with Octanethiol • 98.4 nm Range • Before:100511AE, exposed to laser for one minute • After: 100511AF, cooled for five minutes • +.5 V, 1.001 C, P=10;9, I=10;9, Res:256, 256

  18. Au(111) with Octanethiol • 67.3 nm Range • Before: 100511AG, 1 minute exposed to laser • After: 100511AH, 5 minutes cooling • +.5 V, 1.001 C, P=7, I=7, Res: 256;256

  19. Au(111) with Octanethiol • 87.5 nm Range • Before: 102011AK, 50 seconds exposed to laser • After: 102011AL, 5 minutes cooling • +.5 V,1,001 C, P=10, I=10, Res: 256;256

  20. Au(111) with Octanethiol • 90.61 nm Range • Before: 110311AD, 1 minute exposed to laser • After: 110311AE, 5 minutes cooling • +.5 V, 1.001 C, Res: 256;256, I=10, P=10

  21. Au(111) with Octanethiol • 90.61 nm Range • Before: 110411AD, exposed to laser for one minute • After: 110411AE, five minutes cooling • +.5 V, 1.001 C, Res: 256;256, I=10, P=10

  22. Au(111) with Octanethiol • 78.1 nm Range • Before: 111111AE, exposed to Laser for one minute • After: 111111AF, five minutes cooling • +.5 V, 1.001 C, Res: 256;256, P=8,I=8,

  23. Au(111) with Octanethiol • 100.78 nm Range • Before: 111711AE, exposed to laser for one minute • After: 111711AF, five minutes cooling • +.5 V, 1.001 C, Res: 256;256, I=10, P=10