Soldering Materials. Prepared by: Dental Materials Department Yenepoya Dental College, Yenepoya University, Mangalore. Terminology. Welding two pieces of metal are joined together directly (generally without adding a third metal)

doloresc
Télécharger la présentation

Soldering Materials

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Soldering Materials Prepared by: Dental Materials Department Yenepoya Dental College, Yenepoya University, Mangalore.

  2. Terminology • Welding • two pieces of metal are joined together directly (generally without adding a third metal) • The metal pieces are heated to a high enough temperature so they attach to each other. • Soldering and Brazing • two pieces of metal are joined by adding a third metal • Temp. < 425oC  Soldering • Temp. > 425oC  Brazing • In dentistry, it is most commonly called soldering although the temp. used is above 425oC.

  3. Types of Solders • Soft solder: lead-tin alloys, low melting range (< 260oC) • Known as “plumber’s” solder • Hard solder: high melting range, requires special melting methods • Gold-based solders: good tarnish and corrosion resistance, extensively used in crown and bridge applications • Silver-based solders: commonly used in orthodontic appliances

  4. Ideal solder • Ease of flow at relatively low temperature • Sufficient fluidity to freely flow when melted • Strength compatible with that of the structure being soldered • Acceptable color to give an inconspicuous joint • Resistance to tarnish and corrosion • Resistance to pitting during heating and application

  5. Composition of Dental Gold Solders *Fusion temp. should be at least 50oC below the solidus temp. of the parent (or substrate) alloys.

  6. Mechanical Properties of Dental Gold Solders

  7. Techniques of Dental Soldering • Free-hand soldering • Used in assembling orthodontic and other appliances • Investment soldering • Used in assembling bridges and similar restorations

  8. Soldering Torch

  9. Parent Alloy  granular structure Solder  granular structure Wire  fibrous structure