CHAPTER 14

CHAPTER 14. Electrical Properties Of Materials. 14-1. Electric Conduction – Classical Model. Metallic bonds make free movement of valence electrons possible. Outer valence electrons are completely free to move between positive ion cores.

elizabeth-stout
Télécharger la présentation

CHAPTER 14

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. CHAPTER 14 Electrical Properties Of Materials 14-1

  2. Electric Conduction – Classical Model • Metallic bonds make free movement of valence electrons possible. • Outer valence electrons are completely free to move between positive ion cores. • Positive ion cores vibrate with greater amplitude with increasing temperature. • The motion of electrons are random and restricted in absence of electric field. • In presence of electric field, electrons attain directed drift velocity. 14-2

  3. Ohm’s Law • Ohm’s law states that electric current flow I is directly proportional to the applied voltage V and inversely proportional to resistance of the wire. i = V/Rwhere i = electric current (A) V = potential difference (V) R = resistance of wire (Ω) • Electric resistivity ρ = RA/l where l = length of the conductor and A = Cross-sectional area of the conductor. • Electric Conductivity σ = 1/ ρ • Microscopic Ohm's law J = E/ ρ J= Current density A/m2 E = electric field V/m Figure 13.3 14-3

  4. Drift Velocity of Electrons • Electrons accelerate when electric field E is applied and collide with ion cores . • After collision, they accelerate again. • Electron velocity varies in a saw tooth manner. • Drift velocityVd = μE where μ = electron mobility m2/(V.s) • Direction of current flow is apposite to that of electron flow. Figure 13.4 14-4

  5. Electrical Resistivity • Electrical resistivity ρtotal = ρT + ρr • ρT = Thermal component : Elastic waves (phonons) generated due to vibration of electron core scatter electrons. • Resistivity increases with temperature. • Alloying increases resistivity. • ρr= Residual component : Due to structural imperfections like dislocations. • ρT = ρ0C(1+αTT) ρ0C = Resistivity at 00C αT = Coefficient of resistivity. T = Temperature of the metal Figure 13.7 14-5

  6. Energy Bond Model of Electric Conduction • Valence electrons are delocalized, interact and interpenetrate each other. • Their sharp energy levels are broadened into energy bands. • Example:- Sodium has 1 valence electron (3S1). If there are N sodium atoms, there are N distinct 3S1 energy levels in 3S band. • Sodium is a good conductor since it has half filled outer orbital Figure 13.11 14-6

  7. Energy Band Model for Insulators • In insulators, electrons are lightly bound. • Large energy gap Eg Separates lower filled valence band and upper empty conduction band. • To be available for conduction, the electron should jump the energy gap. Figure 13.14 14-7

  8. Conduction in Intrinsic Semiconductors • Semiconductors: Conductors between good conductors and insulators. • Intrinsic Semiconductors: Pure semiconductors and conductivity depends on inherent properties. • Example: Silicon and Germanium – each atom contributes 4 valence electrons for covalent bond. • Valence electrons are excited away from their bonding position when they are excited. • Moved electron leaves a hole behind. Figure 13.16 14-8

  9. Electrical Charge Transport in Pure Silicon • Both electrons and holes are charge carriers. • Hole is attracted to negative terminal, electron to positive terminal. • Valence electron ‘A’ is missing – Hole • Valence electron ‘B’ moves to that spot due to the electric field leaving behind a hole. • Movement of electrons is apposite to electric field. Figure 13.19 Figure 13.18 14-9

  10. Quantitative Relationship of Electrical Conduction • J = nqVn* + PqVp* • Dividing by electric field E = J/σ • Vn/E and Vp/E are electron and hole mobilities μn, μp σ = nq μn + Pq μp n = p = ni Therefore σ = niq(μn+ μp) n = number of conduction electrons per unit volume. P = number of conduction holes per unit volume. q = absolute value of electron or hole charge = 1.6 x 10-19C Vn, Vp = drift velocities of electrons and holes. 14-10

  11. Effect of Temperature on Intrinsic Semiconductors • The conduction band is completely empty at 00K. • At higher temperatures, valence electrons are excited to conduction bands. • Conductivities increase with increasing temperature. ni= Concentrations of electrons having energy to enter conduction band. E= energy gap. Eav = average energy across gap. K = boatman's constant. T = temperature, K. σ0 = constant depending on the mobility. Since Since Or, 14-11

  12. Extrinsic Semiconductors • Extrinsic semiconductors have impurity atoms (100-1000 ppm) that have different valance characteristics. • n – type extrinsic semiconductors: Impurities donate electrons for conduction. • Example:- Group V A atoms ( P, As, Sb) added to silicon or Ge. Figure 13.22 Figure 13.21 14-12

  13. P-Type Extrinsic Semiconductors • Group III A atoms when added to silicon, a hole is created since one of the bonding electrons is missing. • When electric field is applied, electrons from the neighboring bond move to the hole. • Boron atom gets ionized and hole moves towards negative terminal. • B, Al, provide acceptor level energy and are hence called acceptor atoms. • Doping: Impurity atoms (dopants) are deposited into silicon by diffusion at 11000C. Figure 13.23 14-13

  14. Effect of Doping on Carrier Concentration • The mass action law: np = ni2 where ni (constant) is intrinsic concentration of carriers in a semiconductor. • Since the semiconductor must be electrically neutral Na + n = Nd + p where Na and Nd are concentrations of negative donor and positive acceptors. • In a n-type semiconductor, Na = 0 and n>>p hence nn = Nd and pn = ni2/nn=ni2/Nd np = ni2/pp = ni2/Na Table13.5 14-14

  15. Carrier Concentration • For Si at 300K, intrinsic carrier concentration ni=1.5 x 1016 carier/m2 • For extrinsic silicon doped with arsenic nn = 1021 electrons/m3 pn = 2.25 x 1011 holes/m3 • As the concentration of impurities increase , mobility of carriers decrease. Figure 13.26 14-15

  16. Effect of Temperature on Electrical Conductivity • Electrical conductivity increases with temperature as more and more impurity atoms are ionized. • Exhaustion range: temperature at which donor atom becomes completely ionized . • Saturation range: Acceptor atoms become completely ionized. • Beyond these ranges, temperature does not change conductivity substantially. • Further increase in temperature results in intrinsic conduction becoming dominant and is called intrinsic range. Figure 13.27 14-16

  17. Semiconductor Devices – pn Junction • pn junction if formed by doping a single crystal of silicon first by n-type and then by p type material. • Also produced by diffusion and impurities. • Majority carriers cross over the junction and recombine but the process stops later as electrons repelled by negative ions giving rise to depleted zones. • Under equilibrium conditions, there exists a barrier to majority carrier flow. Figure 13.29a Figure 13.30b 14-17

  18. Reverse and Forward Biased pn Junction • Reverse biased: n-type is connected to the positive terminal and p-type to negative. • Majority carrier electrons and holes move away from junction and current does not flow. • Leakage current flows due to minority carriers. • Forward biased: n-type is connected to negative terminal and p-type to positive. • Majority carriers are repelled to the junction and recombine and the current flows. Figure 13.32 Figure 13.33 Figure 13.31 14-18

  19. Application of pn Junction Diode • Rectifier Diodes: Converts alternating voltage into direct voltage (rectification). • When AC signal is applied to diode, current flows only when p-region is positive and hence half way rectification is achieved. • Signal can be further smoothened by using electronics. Figure 13.34 14-19

  20. Breakdown Diodes (Zener Diodes) • Zener diodes have small breakdown currents. • With application of breakdown voltage, in reverse bias, reverse current increases rapidly. • Electrons gain sufficient energy to knock more electrons from covalent bonds. • These are available for conduction in reverse bias. Figure 13.36 14-20

  21. Bipolar Junction Transistor • BJT consists of two pn junctions occurring sequentially on a single crystal. • Can serve as current amplifier. • Emitter: n-type emits electrons. • Base: p-type, o.1mm thick, controls flow of charge. • Collector: n-type, collects charge carrier. • Emitter base junction is forward biased and collector base junction is reverse biased. • Small base current can be used to control large collector current. Figure 13.37 Figure 13.38 14-21

  22. Microelectronics • Microelectronic planar bipolar transistors: Relatively large island of n-type silicon is formed first in silicon substrate. • Smaller island of p and n type silicon are created on larger n type island. Figure 13.39 14-22

  23. Microelectronic Planar Field-Effect Transistor • MOSFET: Metal oxide semiconductor field effect transistor – compact and cheap. • Two islands of n-type silicon are created in a substrate of p-type silicon. • Between n-type silicon of source and drain there is a p type region. • A surface layer of SiO2 is formed on the p region and another layer of polysilicon on SiO2 layer Figure 13.40 14-23

  24. MOSFET (Cont..) • Electrons will flow between source and drain if there is positive voltage difference between then. • MOSFET has capability of current amplification. Figure 13.41 14-24

  25. Fabrication of Microelectric Integrated Circuits • Photolithography: The process by which microscopic pattern is transferred from a photomask to the silicon wafer surface. • wafer is coated with photoresist. • Then exposed to ultra- violet light through photomask. • Pattern of photoresist is left where mask is transparent. • Wafer is immersed in hydrofluoric acid. • Photoresist pattern is removed by chemicals. Figure 13.45 14-25

  26. Diffusion Technique • Impurity atoms are diffused into silicon wafers at 11000C. • Thin silicon dioxide patterns serve as masks to prevent dopant atoms from penetrating into silicon. • High concentration of dopant is deposited near surface in predeposit step. • In drive-in diffusion step, the wafers are placed in high temperature furnace and necessary concentration of dopant atoms at particular depth is attained. Figure 13.46a 14-26

  27. Ion Implantation Technique • Carried out at room temperature. • Dopant atoms are ionized and accelerated to high energies through a high potential difference of 50-100 KV. • On striking, ions embed in Si. • Photoresist or SiO2 mask is used to mask desired regions. • Damage to Si lattice is caused but can be healed by annealing. Figure 13.46b 14-27

  28. MOS Integrated Circuit Fabrication • SiN4 is deposited by CVD. • Boron ions are implanted to suppress unwanted conduction. • SiO2 layer is grown in inactive regions. • SiN4 is removed by etchants. • Insulating layer is deposited on wafer by CVD. • Al is deposited on wafer. • Protective layer is deposited on entire surface. Figure 13.47 14-28

  29. Complimentary Metal Oxide Semiconductor (MOS) • CMOS: Circuits containing both types of MOSFETs (NMOS and PMOS). • Made by isolating all NMOS devices with islands of p-type material. • Used in LSI circuits in microprocessors and computer memories. Figure 13.49 14-29

  30. Compound Semiconductors • MX semiconductors are major semiconducting compounds. • As molecular mass increases energy band gap decreases and electron mobility increases. • Increased ionic bonding character causes energy bond gap to increase and electron mobility to decrease. • Example: Gallium arsenide: (GaAs) • Higher mobility • GaAs devices have better radiation resistance. Figure 13.49 14-30