ARGUS 54 - Optical Sputter Coater Vacuum Process Technology LLC Dr. Keqi Zhang & Ralph Faber

ARGUS 54 - Optical Sputter Coater Vacuum Process Technology LLC Dr. Keqi Zhang & Ralph Faber May 1, 2013. Motivations:

fauve
Télécharger la présentation

ARGUS 54 - Optical Sputter Coater Vacuum Process Technology LLC Dr. Keqi Zhang & Ralph Faber

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. ARGUS 54 - Optical Sputter Coater Vacuum Process Technology LLC Dr. Keqi Zhang & Ralph Faber May 1, 2013

  2. Motivations: • Offer a deposition tool for optical coating industry that combines the advantages of both e-beam evaporation (large area, fast rate) and IBS deposition (stable process, higher film quality). Approaches: • Plasma enhanced pulsed DC magnetron sputtering • Basic concept is based on a 54-inch chamber with a planetary system that contains six 16-inch planets.

  3. Key Performances / Features: • Sputtered deposition of multilayers of metals, and metal oxides • Large area, fast deposition rate • 6 x 16-inch planets • Rate: Ta2O5/Nb2O5: 5Å/s, SiO2: 6Å/s • Uniformity: typical ±1.0%, goal: ±0.5% • Thickness control • Standard: quartz crystal, time power • Optional: through-the-planet optical monitoring (Single Wavelength or Broad Band)

  4. Optical Sputter Coater Pulsed DC ion / plasma enhanced Materials: Ta2O5/SiO2 Very stable and repeatable process: Deposition rate: 5.0Å/s --- Ta2O5 6.0Å/s --- SiO2

  5. Optical Sputter Coater

  6. Single layer Ta2O5, 5.0 Å/s

  7. Single layer SiO2, 6.0Å/s

  8. Single layer uniformity across a 16-inch planet: < ±1%

  9. Uniformity of a LP filter across a 16-inch planet (spectrally measured)

  10. Uniformity of a LP filter across a 16-inch planet (Normalized)

  11. 550nm Longpass Filter, 30 layers

  12. Coating examples : 72-layer SP (Ta2O5/SiO2 , 5.7µm)Backside uncoated

  13. Coating examples : 37-layer GFF (Ta2O5/SiO2, 3.8µm)Backside uncoated

  14. Coating examples: 14-layer BBAR (Ta2O5/SiO2)

  15. Coating examples: 10-layer Dual-band AR (Ta2O5/SiO2)

  16. Coating examples: 58-layer IR cut filter (Ta2O5/SiO2)

  17. IR Cut Filter Made by a Competitor’s Coater

  18. Coating examples: IR cut filter Argus’54 Competitor’s

  19. Coating examples: 104-layer WB(Ta2O5/SiO2, 7.9µm)

  20. Coating examples: 224-layer WB(Ta2O5/SiO2, 23µm)

  21. Coating examples: 80-layer WB(Ta2O5/SiO2, 7.1µm)Backside uncoated

  22. Coating examples: 52-layer Longpass(Ta2O5/SiO2, 3.0µm)Backside uncoated

  23. Current status: • Optical properties: excellent • Absorption: low • Scattering: low • Mechanical properties • Dense, durable film • Film stress: 230 – 300MPa, compressive • Film uniformity • Less Than ±0.5% on a 16-inch planet • High throughput; unparalleled process stability

  24. Platform Comparison

  25. Products and Applicationsfor the Argus Optics System