1 / 27

Skin layer of BiFeO 3 single crystals http://arxiv.org/abs/1012.2306

Skin layer of BiFeO 3 single crystals http://arxiv.org/abs/1012.2306. X. Marti, V. Holy Charles University, Prague P. Ferrer ESRF, Grenoble J. Herrero-Albillos BESSY, Berlin J. Narvaez, G. Catalan CIN2, Barcelona N. Barrett, CEA, Gif- sur -Yvette M. Alexe MPI, Halle.

gerik
Télécharger la présentation

Skin layer of BiFeO 3 single crystals http://arxiv.org/abs/1012.2306

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Skin layer of BiFeO3 single crystals http://arxiv.org/abs/1012.2306 X. Marti, V. Holy Charles University, Prague P. Ferrer ESRF, Grenoble J. Herrero-Albillos BESSY, Berlin J. Narvaez, G. Catalan CIN2, Barcelona N. Barrett, CEA, Gif-sur-Yvette M. Alexe MPI, Halle xavi.mr@gmail.com SKIN BiFeO3 (AF, FE) = BULK And a general methodology to study skin layers by X-ray grazing incidence diffraction xavi.mr@gmail.com ISIF, Cambridge, AUG 2011

  2. Required: tuneable information depth Ei Snell’s law Critical angle Grazing incidence αi BiFeO3 http://henke.lbl.gov/optical_constants/

  3. Required: tuneable information depth Ei Snell’s law Critical angle Grazing incidence αi BiFeO3 http://henke.lbl.gov/optical_constants/

  4. Refraction is relevant at very low incidence angles To circumvent refraction we proposed scanning both energy and incidence angle

  5. Outline Methodology for energy-dependant grazing incidence diffraction Use on BiFeO3 single crystals Complementary experiments Conclusions

  6. Required: excellent surface of your materials Atomic force microscopy Laboratory X-ray reflectivity Critical angle ~ 0.3 Interface roughness 1.3 nm Peak-to-valley ~ 1 nm Roughness RMS: 0.73 nm

  7. Required: BiFeO3 is a good single crystal Rhombohedral a = 3.964 Å angle = 89.418 °

  8. Caution: BiFeO3 ferroelastic domains BiFeO3(001) Interplanar distance Identical planes point in many directions The interplanar distances are the same

  9. Caution: BiFeO3 ferroelastic domains BiFeO3(001) Identical planes point in many directions The interplanar distances are the same

  10. “Information” in X-ray diffraction is • (#1) Periodicities • (#2) Directions The inter-planar distances are a fingerprint of each material/phase/skin

  11. “Information” in X-ray diffraction is • (#1) Periodicities • (#2) Directions Ei αi Information depth: sample surface “Information itself”: crystal planes BiFeO3 The inter-planar distances are a fingerprint of each material/phase/skin We will investigate the set of interplanar distances in the skin and in the bulk, but we skip the orientation of crystal planes

  12. Technical issue 1/2 (hkl)2 perpendicular direction Two exit angles: αf , Ψ (i.e. latitude, longitude) Ei BiFeO3 αi Primary beam We only align L to be perpendicular to the surface (information depth) Each location in the real space (Ψ, αf) corresponds to a interplanar distance

  13. Technical issue 1/2 (hkl)2 Z: perpendicular to surface Two exit angles: αf , Ψ (i.e. latitude, longitude) Ei BiFeO3 αi Primary beam X Y Pseudocubic reciprocal space coordinates : qx = K * [ cos(αf) * cos(Ψ) - cos(αI) ] ~ H qy = K * [ cos(αf) * sin(Ψ) ] ~ K qz = K * [ sin(αf) + sin(αI) ] ~ L K = 2*π/λ Exact Pseudocubic approximation

  14. Technical issue 1/2 (hkl)2 Z: perpendicular to surface 3-D mesh Ei BiFeO3 αi Primary beam X Y Pseudocubic reciprocal space coordinates : qx = K * [ cos(αf) * cos(Ψ) - cos(αI) ] ~ H qy = K * [ cos(αf) * sin(Ψ) ] ~ K qz = K * [ sin(αf) + sin(αI) ] ~ L K = 2*π/λ Exact Pseudocubic approximation

  15. Technical issue 2/2 Refraction is relevant at very low incidence angles Enlarges out of plane lattice parameters To circumvent refraction we propose scanning different energies at fixed incidence angle Measurement plan: 3-D mesh at two energies and at two incidence angles

  16. Measured Corrected (hkl)2 3-D mesh Maps of (102) and (102) reflections Each pixel is one inter-planar distance Skin layer of BiFeO3 exists The inter-planar distances are different Coincidence after 2 different experiments

  17. All possible [-2 -1 0 1 2] permutations(combinations,3) x4 ferroelastic domains type-(111)

  18. 3:0,-1,2 0.56858...0.0051273,0.25828,0.50651 1:-1,0,2 0.56859...-0.0024343,0.25834,0.50651 4:1,0,2 0.56405...0.0076131,0.24809,0.50651 2:0,1,2 0.56409...-0.0051267,0.24823,0.50651 At the region we measured there are only 4 peaks But only two Q’s were expected!!!

  19. Skin and bulk are in-plane coherent

  20. Skin and bulk are in-plane coherent Red rectangle must be the same Possible changes: α = β, or c

  21. Elongation of c by 0.8% The distortion angle is preserved The skin is triclinic

  22. Elongation of c by 0.8% The distortion angle is preserved The skin is triclinic

  23. X-ray diffraction Capacitance Temperature dependence The skin has its own phase transitions Ac anomalies seen in 3 samples by 3 different growers !!! Independent of polishing process

  24. Concluding remarks We have observed a skin layer in BiFeO3 single crystals Out of plane parameter expands 0.2% in the topmost interface (~10 nm) The skin has its own phase transitions Methodology: 1) Use Q-histograms as fingerprints 2) Tune both energy and angle in “grazing incidence” Acknowledgements H. Schmidt, P. Jégou Spanish Ministerio de Ciencia e Innovación (PI201060E013), Consejo Superior de InvestigacionesCientíficas (PIE 200960I187), the German Science Foundation (Grant SFB762), Ministry of Education of Czech Republic (MSM0021620834), the Grant Agency of the Czech Republic (P204/11/P339) SKIN BiFeO3 (AF, FE) = BULK

  25. Thank you ! SKIN BiFeO3 (AF, FE) = BULK xavi.mr@gmail.com