ANALIZA FREZAL, ZAŠČITENIH S TRDIMI PVD-PREVLEKAMI

ANALIZA FREZAL, ZAŠČITENIH S TRDIMI PVD-PREVLEKAMI ANALYSIS OF MILLERS PROTECTED WITH HARD PVD COATINGS. Setnikar Franc, inž. str., Institut "Jožef Stefan", Jamova 39, Ljubljana, Slovenija dr. Marica Prijanovič Tonkovič, Višja strokovna strojna šola, Novo mesto, Slovenija

holland
Télécharger la présentation

ANALIZA FREZAL, ZAŠČITENIH S TRDIMI PVD-PREVLEKAMI

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. ANALIZA FREZAL, ZAŠČITENIH S TRDIMI PVD-PREVLEKAMI ANALYSIS OF MILLERS PROTECTED WITH HARD PVD COATINGS Setnikar Franc, inž. str., Institut "Jožef Stefan", Jamova 39, Ljubljana, Slovenija dr. Marica Prijanovič Tonkovič, Višja strokovna strojna šola, Novo mesto, Slovenija dr. Peter Panjan, Institut "Jožef Stefan", Jamova 39, Ljubljana, Slovenija

  2. Cilj naloge: • zmanjšati čas obdelave, • povečati kvaliteto površine obdelovanca • povečati produktivnost, • postati konkurenčen na tržišču.

  3. Potek dela Preiskovali smo orodje obstojnost steblastega frezala s štirimi rezalnimi robovi. Frezalo je: • imelo premer 10 mm, • zaščiteno je bilo z različnimi trdimi PVD-prevlekami, • namenjeno je suhi obdelavi (obdelava brez brez hladilno-mazalnih tekočin), • material je orodnega jekla za delo v vročem.

  4. U kat S N S N2 N2 N2 N2 N2 N2 N2 N2 N2 N2 Plazma Delovni plin (Ar+Kr) Ar Ar Ar Ar+ Ar+ Ar+ Ar+ Ar+ Ar+ Ar+ Ar+ Ar+ Ti Ti+ Ti+ Ti+ Ti+ Ti+ Ti+ Ti+ Ti Ti Ti+ Ti Ti Reaktiven plin e.g. N2 Magnetne silnice Podlaga Nosilec podlag U Bi Teoretičen del naprševanja CC800 (CemeCon)

  5. Optimalen prenos toplote odrezek odrezek Q Q S1 S2 Q Q Q TiAlN tot2 tot1 tot1 obdelovanec obdelovanec Q Q W1 W2 Orodje z TiAlN prevleko Orodje brez prevleke v c1 v c2 Zaradi majhnega koeficienta toplotne prevodnosti, se pri orodjihzaščitenih s TiAlN prevleko večina toplote odvede v odrezek Teoretičen del odvoda toplote

  6. Kemična sestava obdelovanca Tabela 1: Kemična sestava jekla UTOP MO 6 Table 1: Chemical composition of steel UTOP MO 6

  7. Geometrija frezala Slika 1: Geometrija frezala Picture 2: Geometyof the miller

  8. Frezalni stroj CNC, DECKEL MACHO CAD - modeliranje, INVENTOR CAM – NC programiranje, Hyper MILL Šoba za zrak frezalo obdelovanec Tehnologijafrezanja Slika 2: Rezkanje s frezalom Picture 2: Milling with a miller

  9. Vrste frezal oz. preizkušancev Tabela 2: Vrste frezal Table 2: Types of millers * krušenje konice rezilnega roba na začetku frezanja, a) vrednost EDS je orientacijska

  10. REZULTAT MERITEV • Pri frezalih 10 proizvajalca B in 15 proizvajalca D je prišlo do krušenja osnovnega materiala. • Izmerili smo trdoto po Vickersu HV in vtisni modul EIT. Graf 1: Rezultati meritev trdote in vtisnega modulaGraph 1: Measurements results of the hardness and indentation modulus

  11. Frezalo 1 (A) po 65 m Frezalo 1 (A) po 97 m Frezalo 1 (A) po 45 m Frezalo 2 (A) po 45 m Frezalo 2 (A) po 65 m Frezalo 2 (A) po 97 m REZULTAT MERITEV Slika 3: Optičnomikroskopski posnetki čelne proste ploskve na frezalih 1 in 2 proizvajalca A ; 20-kratna povečava Picture 3: Optical microscopic pictures of the front relief surface on millers 1 and 2 of the manufacturer A; 20-times magnified

  12. Meja med prevleko in karbidno trdino TiAlN Karbidna trdina obrabljeno obrabljeno Frezalo 1 (A) po 97 m Frezalo 2 (A) po 97 m REZULTAT MERITEV Slika 4: SEM-posnetek frezala 1 in 2 proizvajalca A; 500-kratna povečava Picture 4: SEM-print of the miller 1 and 2 of the manufacturer A; 500-times magnified

  13. REZULTAT MERITEV Tabela 3: Sestava in debelina zaščitne prevleke ter povprečna velikost karbidnih zrn Table 3: Composition and thickness of the protective coating and average size of the carbide grain

  14. TiAlN (54/46%) TiAlN (57/43) Razpoka Karbidna trdina TiN (72/28) Krater Frezalo 1 (A) Frezalo 17 (E) REZULTAT MERITEV Slika 6: SEM-posnetek prečnega obrusa trde prevleke, s katero sta bili zaščiteni frezali 1 (A) in17 (E); 500-kratna povečava Picture 6: SEM prints of the cross section of specimen with the hard coating with which the millers 1 (A) in 17 (E) were protected; 500-times magnified

  15. REZULTAT MERITEV • V projektni nalogi smo preizkušali frezala zaščitena s TiAlN-prevleko. • Prevleka obdrži veliko trdoto vse do 800 °C. • SEM-posnetki rezilnega roba kažejo večjo obrabno obstojnost, če ima frezalo poleg TiAlN-prevleke še tanko vmesno plast iz TiN. • Z uvedbo novih materialov za odrezavanje je možno zmanjšati stroške obdelave in povečati proizvodne kapacitete. • Tako postane podjetje bolj konkurenčno, kar je bil tudi cilj našega projektnega dela.

  16. obrabljeno obrabljeno Frezalo 1 (A) po 97 m Frezalo 7 (A) po 20 m Sklepne ugotovitve • Odrezovanje s frezali brez trde zaščitne prevleke nesmiselno in ekonomsko neupravičeno. • Obdelava materialov s trdoto HRc nad 50 s frezalom brez prevleke ni možna. prekritega neprekritega

  17. Na obstojnost prevleke in frezal vpliva kvaliteta karbidne trdine, finozrnata in neporozna. • Razvoj usmerjen v trde prevleke na osnovi CrAlN, večja obrabna obstojnost, visoka trdota v vročem in oksidacijsko obstojna pri temperaturi do 900 °C • Idealna prevleka, še z dodatkom trdega maziva • Dobro poznanje obrabnih procesov • Obdelava z frezali, zaščitenimi z sodobnimi prevlekami, bolj učinkovita, kakovostna ter okolju in zdravju ljudi bolj prijazna.

  18. " Samo kakovost, produktivnost in zadovoljni kupci lahko komurkoli od nas zagotovijo varno službo v podjetju." (Chrysler) Hvala za pozornost. THANK YOU FOR YOUR ATTENTION.