An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Microfabrication of 100 GHz Test Structures Corning Glass Cover Slips: $0.12 each New lithographic mask was designed in order to have the frequency response shifted to the band around 100 GHz. εglass (@100 GHz)= 6.5 Microscope cover slides were chosen as substrate due to low cost and appropriate geometry. Slide thickness is around 250 μm, slide area is 22 mm x 22 mm.

  2. Exact Geometry of Features on the 100 GHz Mask • The following dimensions were calculated using: • Target frequency: 100 GHz. • Previous design (12 GHz) dimensions. • Substrate relative permittivity (6.5) at target frequency.

  3. Exact Geometry of Features on the 100 GHz Mask

  4. Array area: 15 mm x 15 mm Array: 33 x 33 Alignment - 1: Array to Glass (during Fabrication) Alignment - 2: Glass to Glass (Stacking) (during Measurement)

  5. Fabricated Structures • Fabrication at Microelectronics Facility of FORTH, Heraklion. • With Dr. George Konstantinidis. • Method: Image Reversal Lithography(AZ5214) / E-Gun Metal Deposition (5000Å Ag) / Lift-Off