METAKAOLIN ALİ GÜMÜŞ 18926635336

METAKAOLIN ALİ GÜMÜŞ 18926635336. GENERAL DEFINITION. The raw material in the manufacture of Metakaolin is kaolin clay. Kaolin is a fine , white, clay mineral that has been traditionally used in the manufacture of porcelain

mhayden
Télécharger la présentation

METAKAOLIN ALİ GÜMÜŞ 18926635336

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. METAKAOLINALİ GÜMÜŞ 18926635336

  2. GENERAL DEFINITION • The raw material in the manufacture of Metakaolin is kaolin clay. Kaolin is a fine , white, claymineral that has been traditionally used in the manufacture of porcelain • Metakaolin is obtained by keeping the pure clay at about 700 ° C for 30-60 minutes and completely evaporating its bound water. • The particle size of metakaolin is smaller than cement particles, but not as fine as silica fume.

  3. BASIC PROPERTIES • Metakaolin is white. • Itcontains high amounts of amorphous silica. • Itpreventsdurabilityproblemssuch as alkali-silica reaction, sulfate attack and flowering. • It provides impermeability to concrete elements.

  4. GENERAL STRUCTURE OF METAKAOLİN • Composed of 50-55% SiO2 and 45-50 Al2O3 Al2O3.2SiO2.2H2O -> Al2O3.2SiO2 + 2H2O + Enerji -> METAKAOLİN • Its surface area is 1500-2500 cm2/gr similar to cement. • The density of its is approximately 2.5 g/cm3. • Average Grain Size is below 2 Micron.

  5. CHEMICAL COMPOSITION

  6. ADVANTAGES OF METAKAOLIN • In mixtures containing metakaolin, the setting time is shorter as Portland cement hydrates have more surface area and some of the mixing water is absorbed by the clay over time. • Metakaolin increases the strength values • Although metakaolin differs according to its structural properties, it exhibits performance exceeding silica fume when it reaches the appropriate fineness and reactivity.

  7. ADVANTAGES OF METAKAOLIN Metakaolinconverts CH to C-S-H gel whence; • Itprovidestodecreasingpermeability of theconcrete. • Itprecludes alkali-silica gel. • Andthelastmetakaolinreduces C3A present in cement.Therefore reduces the amount of elongation caused by sulfate attack by up to 50%.

  8. DISADVANTAGES OF METAKAOLIN • Metakaolinreduces workability.Due to its clay structure, it increases the water requirement of the mortar. Therefore, a chemical additive (plasticizer) should be added in the mixtures used metakaolin.

  9. References • Metakaolin- Pozzolanic Material For Cement in High StrengthConcreteSanjay N. Patil, Anil K. Gupta, Subhash S. Deshpande • Metakaolin ve Akışkanlaştırıcı Katkı Kullanımının Harçların Mekanik Performansına ve Bazı Durabilite Özelliklerine Etkileri Selçuk TÜRKEL, Melek Müge TEVRİZCİ • MetakaolinJamal M.KhatibOussamaBaalbakiAdel A.ElKordi • Farklı Sınıf Çimento Harcı Üretiminde Metakaolin Katkısı Kullanımının Araştırılması Gökhan Görhan ve Gökhan Kürklü

  10. TEŞEKKÜRLER