1 / 10

Photovoltaics. Lecture 6. CIGS.

Photovoltaics. Lecture 6. CIGS. From previous lecture:. Contacts resistance and recombination. Useful recombination limits. Thickness dependant efficiency. TOM TIEDJE et al., IEEE TRANS. ON EL. DEVICES, VOL. ED-31, NO. 5 , MAY 1984. Photovoltaics. Lecture 6. CIGS.

ohio
Télécharger la présentation

Photovoltaics. Lecture 6. CIGS.

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Photovoltaics. Lecture 6. CIGS. From previous lecture: Contacts resistance and recombination. Useful recombination limits. Thickness dependant efficiency. TOM TIEDJE et al., IEEE TRANS. ON EL. DEVICES, VOL. ED-31, NO. 5 , MAY 1984

  2. Photovoltaics. Lecture 6. CIGS. Few words on amorphous Si: Hydrogen improves properties. Semi-direct band gap, with exponential edges. Absorption up to 2.5 times higher than in crystalline Si.

  3. Photovoltaics. Lecture 6. CIGS. Few words on amorphous Si: Staebler-Wronski Effect: Significant decline in the efficiency of a-Si:H solar cells during first few hundred hours of illumination 1.7eV 1.1eV

  4. Photovoltaics. Lecture 6. CIGS. Cu(Inx,Ga1-x)Se2 (CIGS) solar cells:

  5. Photovoltaics. Lecture 6. CIGS. Solar cells industry: H.S. Ullal and B. von Roedern, NREL/CP-520-42058, September 2007

  6. Photovoltaics. Lecture 6. CIGS. Cu(Inx,Ga1-x)Se2 (CIGS): C b-phase CuIn3Se5 R. Herberholz et al.,Euro. Phys. J. AP 6, 131 (1999)

  7. Photovoltaics. Lecture 6. CIGS. Cu(Inx,Ga1-x)Se2 (CIGS): E (x)[eV] = 1,02 +0,67x + 0,11x(x-1)

  8. Photovoltaics. Lecture 6. CIGS. Cu(Inx,Ga1-x)Se2 (CIGS):

  9. Photovoltaics. Lecture 6. CIGS. Cu(Inx,Ga1-x)Se2 (CIGS):

  10. Photovoltaics. Lecture 6. CIGS. Cu(Inx,Ga1-x)Se2 (CIGS):