Surface micromachining

Surface micromachining. How a cantilever is made:. http://www.darpa.mil/mto/mems. Sacrificial material : Silicon oxide Structural material : polycrystalline Si (poly-Si) Isolating material (electrical/thermal): Silicon Nitride. Silicon oxide deposition. SiH 4 + O 2.

simone-castro
Télécharger la présentation

Surface micromachining

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Surface micromachining How a cantilever is made: http://www.darpa.mil/mto/mems Sacrificial material: Silicon oxide Structural material: polycrystalline Si (poly-Si) Isolating material (electrical/thermal):Silicon Nitride

  2. Silicon oxide deposition SiH4 + O2 LTO: Low Temperature Oxidation process • For deposition at lower temperatures, use • Low Pressure Chemical Vapor Deposition (LPCVD) • SiH4 + O2 SiO2 + 2H2 : 450 oC • Other advantages: • Can dope Silicon oxide to create PSG (phospho-silicate glass) • SiH4 + 7/2 O2 + 2 PH3 SiO2:P + 5 H2O : 700 oC • PSG: higher etch rate, flows easier (better topography) 425-450 oC 0.2-0.4 Torr

  3. Case study: Poly-silicon growth SiH4 Amorphous film 570 oC Crystalline film 620 oC • by Low Pressure Chemical Vapor Deposition • T: 580-650 oC, P: 0.1-0.4 Torr • Effect of temperature • Amorphous  Crystalline: 570 oC • Equi-axed grains: 600 oC • Columnar grains: 625 oC • (110) crystal orientation: 600 – 650 oC • (100) crystal orientation: 650 – 700 oC Kamins,T. 1998 Poly-Si for ICs and diplays, 1998

  4. Poly-silicon growth • Temperature has to be very accurately controlled • as grains grow with temperature, increasing surface • roughness, causing loss of pattern resolution and stresses in • MEMS • Mechanisms of grain growth: • Strain induced growth • - Minimize strain energy due to mechanical deformation, doping … • - Grain growth  time • 2. Grain boundary growth • - To reduce surface energy (and grain boundary area) • - Grain growth  (time)1/2 • 3. Impurity drag • - Can accelerate/prevent grain boundary movement • - Grain growth  (time)1/3

  5. Grains control properties • Mechanical properties • Stress state:Residual compressive stress (500MPa) • - Amorphous/columnar grained structures: Compressive stress • - Equiaxed grained structures: Tensile stress • Thick films have less stress than thinner films • ANNEALING CAN REDUCE STRESSES BY A • FACTOR OF 10-100 • Thermal and electrical properties • Grain boundaries are a barrier for electrons • e.g. thermal conductivity could be 5-10 times lower (0.2 W/cm-K) • Optical properties • Rough surfaces!

  6. Silicon Nitride SiH2Cl2 + NH3 (for electrical and thermal isolation of devices) r: 1016W cm, Ebreakdown: 107 kV/cm • Is also used for encapsulation and packaging • Used as an etch mask, resistant to chemical attack • High mechanical strength (260-330 GPa) for SixNy, provides structural integrity (membranes in pressure sensors) • Deposited by LPCVD or Plasma –enhanced CVD (PECVD) LPCVD: Less defective Silicon Nitride films PECVD: Stress-free Silicon Nitride films x SiH2Cl2 + y NH3 SixNy + HCl + 3 H2 700 - 900 oC 0.2-0.5 Torr

  7. Depositing materialsPVD (Physical vapor deposition) • Sputtering: DC (conducting films: Silicon nitride) RF (Insulating films: Silicon oxide) http://web.kth.se/fakulteter/TFY/cmp/research/sputtering/sputtering.html

  8. Depositing materialsPVD (Physical vapor deposition) • Evaporation (electron-beam/thermal) Commercial electron-beam evaporator (ITL, UCSD)

  9. Electroplating Courtesy: Jack Judy • Issues: • Micro-void formation • Roughness on top surfaces • Uneven deposition speeds • Used extensively for LIGA processing e.g. can be used to form porous Silicon, used for sensors due to the large surface to volume ratio

  10. Depositing materials –contd.- • Spin-on (sol-gel) • e.g. Spin-on-Glass (SOG) used as a sacrificial molding material, processing can be done at low temperatures Dropper Si wafer

  11. Surface micromachining - Technique and issues - Dry etching (DRIE) Other MEMS fabrication techniques - Micro-molding - LIGA Other materials in MEMS - SiC, diamond, piezo-electrics, magnetic materials, shape memory alloys … MEMS foundry processes - How to make a micro-motor

  12. Surface micromachining Carving of layers put down sequentially on the substrate by using selective etching of sacrificial thin films to form free-standing/completely released thin-film microstructures http://www.darpa.mil/mto/mems HF can etch Silicon oxide but does not affect Silicon Release step crucial

  13. Release of MEMS structures • A difficult step, due to surface tension forces: Surface Tension forces are greater than gravitational forces ( L) ( L)3

  14. Cantilever Si substrate Release of MEMS structures • To overcome this problem: • Use of alcohols/ethers, which sublimate, at release step • Surface texturing • Supercritical CO2 drying: avoids the liquid phase 35oC, 1100 psi

  15. A comparison of conventional vs. supercritical drying

  16. Reactive Ion Etching (RIE) DRY plasma based etching http://www.memsguide.com • Deep RIE (DRIE): • Excellent selectivity to mask material (30:1) • Moderate etch rate (1-10 mm/minute) • High aspect ratio (10:1), large etch depths possible

  17. Deep Reactive Ion Etching (DRIE) A side effect of a glow discharge  polymeric species created Plasma processes: Deposition of polymeric material from plasma vs. removal of material Usual etching processes result in a V-shaped profile Bosch ProcessAlternate etching (SF6) +Passivation (C4F8) • Bowing: bottom is wider • Lag: uneven formation

  18. Gas phase Silicon etching • Room temperature process • No surface tension forces • No charging effects • Isotropic XeF2 BrF3 Developed at IBM (1962) Developed at Bell labs (1984) 2 XeF2 + Si  2 Xe + SiF4 4 BrF3 + 3 Si  2 Br2 + 3 SiF4 Cost: $150 to etch 1 g of Si $16 for 1 g of Si Etching rate: 1-10 mm/minute

  19. Micro-molding • For thick films (> 100 mm) • HEXSIL/PDMS, compatible with Bio-MEMS C. Keller et al, Solid state sensor & actuator workshop, 1994 - loss of feature definition after repeated replication - Thermal and mechanical stability

  20. LIGA (LIthographie, Galvanoformung, Abformung) • For high aspect ratio structures • Thick resists (> 1 mm) • high –energy x-ray lithography ( > 1 GeV) • Millimeter/sub-mm sized objects which require precision Mass spectrometer with hyperbolic arms Electromagnetic motor

  21. Technology Comparison Bulk vs. Surface micromachining vs. LIGA

  22. Materials in MEMS Mechanical MEMS (for micro-motors etc.) Si, quartz (SiO2), Si3N4, Ti, Ni, permalloy (NiFe), polycrystalline Si … RF-MEMS (for wireless communications): Compound semiconductors: GaAs, InP, GaN Si, SiO2 … Bio-MEMS (micro-electrode arrays, DNA probes) enzymes, antigen/antibody pairs, DNA, polyimides, hydrogels, plastics, porous Si, C, AgCl…

  23. METALS used for wiring (Al, Cu), etch masks (Cr), structural elements (Al, W) - excellent electrical conductors - prone to fatigue SMA : Shape memory alloys(NiTi: Nitinol) Reversible temperature induced transformation from a stiff austenite phase (Y.S.: 550 MPa) to a ductile martensite (Y. S.: 100 MPa) phase. - used for thermal actuation - Can exert stresses of up to 100 MN/m2 - Maximum operating temperature ~ 70 oC - very slow actuation mechanism Polymers: poly-norbornene

  24. Photoresist (PR) Cr/Au Glass substrate Si oxidation Si SiO2 Pattern PR Si etch (KOH) Etch Cr/Au Pattern & deposit NiFe Etch Glass RIE to release cantilever Remove Cr/Au Magnetic materials • prevalent: Ni, NiFe (permalloy), Co alloys • - Not as widely used as electrostatic actuation • - Needs thick films (10-20 mm); using electro-deposition A magnetically actuated cantilever

  25. New applications demand new materials Silicon Carbide (SiC): structural & isolating layer - mechanically robust, E(500 GPa)  higher resonance frequency - high temperature material (>200 oC) - difficult to shape (chemically inert) - used in micro-gas turbines Diamond: very hard, for electrical isolation - E: 1035 GPa - excellent thermal conductor, easy heat dissipation - difficult to machine, needs oxygen-plasmas - used in Atomic Force Microscope cantilevers GaAs/InP: opto-electronics - good combination of electrical and mechanical properties - high piezo-electric coefficients - sophisticated manufacture for GaAs and InP substrates (Molecular Beam Epitaxy)

  26. Polymers: structurally compliant • - 50 times lower E compared to Si/Silicon nitride • - Can withstand large strains (100%) • Polyimide: used in force sensor, shear stress • sensor skin • Piezoelectrics: have a mechanical response to an • electric field: ZnO, (Pb,Zr)TiO3 • - Large mechanical transduction, force sensors

  27. Silicon is comparable to steel