Crystal Structure MnDC- 3 and MnDC-4

c. a. c. b. Crystal Structure MnDC- 3 and MnDC-4. c. a. b. c. MnDC-3 MnDC - 4. Edge share. Mn-O-Mn connectivity. Corner share. Mn. Mn. Mn. Mn. Mn. Mn. Mn. Mn. b. a. MnDC-3.

taro
Télécharger la présentation

Crystal Structure MnDC- 3 and MnDC-4

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. c a c b Crystal Structure MnDC- 3 and MnDC-4 c a b c MnDC-3 MnDC - 4

  2. Edge share Mn-O-Mn connectivity Corner share Mn Mn Mn Mn Mn Mn Mn Mn b a MnDC-3

  3. Comparison of M2(H2O)[adipate]2 ( M = Mn, Fe) Mn2(H2O)[CO2(CH2)4CO2]2, Fe2(H2O)[CO2(CH2)4CO2]2 ,[adipate n=4 (even number) in M2(H2O)[CO2(CH2)4CO2]2(M= Mn and Fe)] Kim, Y.J.; Jung, D. Y. Inorg. Chem.2000, 39, 1470. Kim, Y.J.; Jung, D. Y. Bull. Korean Chem. Soc.2000, 21, 656. Kim, Y. J.; Lee, E. W.; Jung, D. Y. Chem. Mater.2001, 13, 2684.

  4. Magnetism of MnDC-n (n=3 to 12) 100G 5K-300K SQUID [Wagner and Friedberg model] J = -1.81 ~ -2.04 g = 1.95 ~ 2.01 [Hiller model] J = -1.95 ~ -2.16 g = 1.95 ~ 2.02 (U=coth K-1/K,K=JS(S+1)/kT) (A=2.9167 B=208.04 C=15.543 and X=|J|/2kT)

  5. Mn- Conformation of Terminal Carboxylate Groups Dicarboxylic acid Metal Dicarboxylate Glutaric (odd) Adipic (even) (odd) Mn- -Mn (even) -Mn

  6. Thermal Analyses Obsd. Calcd. Obsd. Calcd(Mn2O3) Compound TH2O wt loss Torganic Residue wt. Loss MnDC-3 225-252 5.1 4.6 345-800 47.3 40.7 MnDC-4 228-248 4.3 4.3 306-800 39.9 37.9 MnDC-5 218-248 4.2 4.1 309-800 37.7 35.5 MnDC-6 220-236 4.1 3.8 302-800 34.0 33.4 MnDC-7 208-233 3.8 3.6 297-800 33.8 31.6 MnDC-8 195-229 3.5 3.4 275-800 32.7 29.9 MnDC-9 190-215 3.4 3.2 295-600 27.9 28.4 MnDC-10 160-200 3.2 3.1 260-600 26.8 27.0 MnDC-11 152-173 2.9 2.9 285-600 23.5 25.8 MnDC-12 145-165 2.8 2.8 275-600 24.2 24.7 Dehydration range N2 flow 10oC/min Mn2(H2O)[CO2(CH2)nCO2]2  Mn2[CO2(CH2)nCO2]2 Mn2O3 150-250 oC 600 oC

  7. Conclusions •  We opened a new series of Mn-dicarboxylate compounds, MnDC- n (n = 3 to 12), which contains tunable interlayer distance using various ,-dicarboxylic acids by hydrothermal synthesis. • The manganese-oxygen connectivity of both even and odd members of MnDC-n, are very similar and the resulting magnetic properties is predominantly antiferromagnetic ascribed to the Mn-O-Mn infinite chains. Acknowledgment We acknowledge financial support from the Electron Spin Science Center at POSTECH, which established as the excellent science research center by the KOSEF.