Deformation and texture

Crystallography. H. K. D. H. Bhadeshia. Deformation and texture. www.msm.cam.ac.uk/phase-trans/books.html. ’. slip direction must lie in slip plane maximum shear stress at 45°. Deihl ’ s rule.

thalassa
Télécharger la présentation

Deformation and texture

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Crystallography H. K. D. H. Bhadeshia Deformation and texture

  2. www.msm.cam.ac.uk/phase-trans/books.html

  3. ’

  4. slip direction must lie in slip plane maximum shear stress at 45°

  5. Deihl’s rule

  6. A non-random distribution of crystal orientations in a polycrystalline sample is said to be textured.

  7. 100 pole figure plotted relative to sample axes

  8. RD 100 pole figure showing “cube” texture TD

  9. pole figure RD TD

  10. Inverse pole figure Due to cubic symmetry, only one triangle needs to be illustrated

  11. Electron back-scattered diffraction

  12. crystallographic structure at fusion line

  13. RD 100 pole figure showing “cube” texture TD