An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. CHAPTER 10 Polymeric Materials 10-1

  2. Introduction to Polymers • Polymers many parts Polymers Plastics Elastomers Thermoplastics Thermosetting Plastics Can be reheated and formed into new materials Cannot be reformed by reheating. Set by chemical reaction. 10-2

  3. Wide range of properties. Minimum finishing. Minimum lubrication. Good insulation. Light weight. Noise Reduction. Plastics - Advantages Remote Control Wafer bands Air intake manifold Figure 7.1 10-3 Royalty-Free/CORBIS. (b) Charles O’Rear/ CORBIS. (c) Tom pantages

  4. Polymerization • Chain growth polymerization: Small molecules covalently bond to form long chains (monomers) which in turn bond to form polymers. • Example: Ethylene • Functionality: Number of active bonds in a monomer. n=degree of Polymerization (DP). (range: 3500-25000 H H C C H H H H C C H H Heat n Pressure Catalyst n Molecular mass of polymer(g/mol) DP = Mass of a mer (g/mer) 10-4

  5. Chain Polymerization - Steps • Initiation: • A Radical is needed. • Example H2O2 • One of free radicals react with ethylene molecule to form new longer chain free radical. In General 10-5

  6. Chain Polymerization – Steps (cont..) • Propagation: Process of extending polymer chain by addition of monomers. • Energy of system is lowered by polymerization. • Termination:- • By addition of termination free radical. • Combining of two chains • Impurities. R CH2 CH2 + CH2 CH2 R CH2 CH2 CH2 CH2 R(CH2 CH2)m + R’(CH2 CH2)n R(CH2 CH2)m R (CH2 CH2)n R’ Coupling of two chains 10-6

  7. Average Molecular Weight • Average molecular weight determined by special physical and chemical techniques. • Example: = average molecular weight of thermoplastics. Mi = Mean molecular weight of each molecular range selected. fi = Weight fraction of the material having Molecular weights of a selected molecular Weight range. = 19,550 1 = 19,550 g/mol 10-7

  8. Structure of Noncrystalline Linear Polymers • Zig-Zag configuration in ethylene due to 109 degree angle between carbon covalent bonds. • Chains are randomly entangled. • Entanglement increases tensile strength. • Branching decreases tensile strength. Figure 7.4 Figure 7.5 10-8 After W. G. Moffatt, G. W. Pearsall, and J. Wulff, “The structure and Properties of Materials,” vol I: “Structure,” Wiley, 1965, p.65,104

  9. Vinyl and Vinylidene Polymers • Vinyl polymers: One of the hydrogen atom is replaced by another atom or group of atoms. • Vinylidene Polymers:Both hydrogen of carbon are replaced by another atom or group of atoms. Figure 7.6 Figure 7.7 10-9

  10. Homopolymer and Copolymers • Homopolymers: Polymer chain is made up of single repeating units. Example:AAAAAAAA • Copolymers: Polymer chains made up of two or more repeating units. • Random copolymers: Different monomers randomly arranged in chains. Eg:- ABBABABBAAAAABA • Alternating copolymers: Definite ordered alterations of monomers. Eg:- ABABABABABAB • Block copolymers: Different monomers arranged in long blocks. Eg:- AAAAA…….BBBBBBBB…… • Graft copolymers: One type of monomer grafted to long chain of another. Eg: AAAAAAAAAAAAAAAAAAA B B B B B B 10-10

  11. Other Methods of Polymerization • Stepwise Polymerization: Monomers chemically react with each other to produce linear polymers and a small molecule of byproduct. • Network polymerization: Chemical reaction takes place in more than two reaction sites (3D network). Figure 7.10 Figure 7.11 10-11

  12. Industrial Polymerization Raw Materials: Natural gas, Petroleum and coal Granules, pellets, powders or liquids. Polymerization • Bulk polymerization : • Monomer and activator • mixed in a reactor and • heated and cooled as desired • Solution polymerization: Monomer • dissolved in non-reactive solvent • and catalyst. • Suspension polymerization: monomer • and catalyst suspended in water. • Emulsion polymerization: Monomer • and catalyst suspended in water along with emulsifier. Figure 7.12 10-12 After W. E. Driver, “Plastics Chemistry and Technology,” Van Nostrand Reinhold, 1979, p.19

  13. Solidification of Thermoplastics. • There is no sudden change in specific volume on cooling in noncrystalline thermoplastics. • In crystalline thermoplastics, sudden decrease in specific volume occurs due to more efficient packing of polymer chains. Tg = glass transition temperature. Glass brittle below above Rubbery Tg Tg for polyethylene is –1100C For PVC it is 820C Figure 7.14 10-13

  14. Structure of Partly Crystalline Thermoplastics • Longest dimension of crystalline region is 5-50 nm. • Fringed micelle model: Long polymer chains of 5000 nm wandering successively through a series of disordered and ordered region. • Folded chain model: sections of molecular chains folding on themselves. Polyethylene-folded chain Figure 7.17 Figure 7.16 After F. Rodriguez, “priciples of Polymer Systems,” 2nd ed., McGraw-Hill, 1982,p.42 After R. L. Boysen, Olefin Polymers, in “Encyclopedia of Chemical Technology,” vol. 16, Wiley, 1981, p.405. 10-14

  15. Stereoisomerism in Thermoplastics • Stereoisomer:- Same chemical composition but different structural arrangements. • Atactic stereoisomer:- Pendent methyl group of polypropylene is randomly arranged on either side of main carbon chain. • Isotactic stereoisomer:- The pendent methyl group is always on same side of the carbon chain. • Syndiotactic stereoisomer:- The pendant group regularly alternates from one side of the chain to the other side. Figure 7.19 10-15 After G. Crepsi and L. Luciani, in “Encyclopedia of Chemical Technology,” vol. 16, Wiley, 1982, p.454.

  16. Processing of Plastic Materials • Injection Molding: uses reciprocating screw mechanism. • More uniform delivery of melt for injection. • High quality, low labor cost, but high initial cost. Figure 7.22 Figure 7.21 10-16 After J. Brown, “ Injection Molding of Plastic Components,” McGraw-Hill, 1979, p.28.

  17. Extrusion, Blow molding and Thermo Forming • Extrusion: Melted plastic forced by a rotating screw through a opening and used to produce pipes, rods etc. • Blow molding: Compressed air is blown into heated cylinder or pipe of plastic to press it against the wall of mold. • Thermoforming: heated plastic sheet is forced into contours of a mold by pressure. Figure 7.23 10-17 After H. S. Kauffman and J. J. Falcetta(eds.), “Introductin to Polymer Science and Technology” Wiley, 1977, p.462.

  18. Processes for Thermosetting • Compression molding: Pressure is applied on heated plastic by upper mold and the molten plastic fills the cavities. • Low initial cost, simple. • Less wear and abrasion of molds. • Difficult to mold complex parts • Creates flash (spills). Figure 7.25 10-18 After B. B. Seymour, Plastics Technology, in “ Encyclopedia of Chemical Technology,” vol. 15, Wiley, 1968, p.802.

  19. Transfer Molding • A plunger forces plastic resin, placed outside mold, into mold cavities through runners and gate. • No flash formed. • Multiple parts at a time. • Can be used for small and intricate parts. • Injection molding is also used to process thermosetting plastics. • Special heating-cooling jackets are added to standard injection molding machine. Figure 7.26 10-19 Courtesy of Plastics Engineering Co., Sheboygan, Wisc.

  20. General Purpose Thermoplastics • Polyethylene, polyvinyl chloride (PVC) polypropylene and polyesters account for most plastic materials sold. Table 7.2 10-20 Materials Engineering, May 1972

  21. Polyethylene • Clear to whitish translucent thermoplastic. • Types • Low density • High Density • Linear low density • Applications: containers, insulation, chemical tubing, bottles, water pond liners etc. Figure 7.28 Table 7.3 10-21

  22. Polyvinyl Chloride and Copolymers • PVC is amorphous, does not recrystallize. • Chlorine atoms produce large dipole moments and also hinder electrostatic repulsion. • PVC homopolymer has high strength (7.5 to 9 KSI) and is brittle. • Compounding of PVC: Modifies and improves properties. • Plasticizers: Impart flexibility. Eg – Phthalate. • Heat Stabilizers: Prevent thermal degradation. Eg – lead and tin compounds. • Lubricants: Aid in melt flow of PVC. Eg – Waxes and fatty esters. • Fillers: Lower the cost. Eg – Calcium Carbonate. • Pigments : Give color. 10-22

  23. Polypropylene • Low density, good chemical resistance, moisture resistance and heat resistance. • Good surface hardness and dimensional stability. • Applications: Housewares, appliances, packaging, laboratory ware, bottles, etc. • Methyl group substitute every other carbon • atom in carbon polymer chain. • High melting (165-1770Cand heat deflection • temperature. H H C C H CH3 n 10-23

  24. Polystyrene • Phenyl ring present on every other • carbon atom. • Very inflexible, rigid, clear and brittle. • Low processing cost and good dimensional • stability. • Poor weatherability and easily attacked • by chemicals. H H C C H • Applications: Automobile interior parts, dials and knobs of appliances and housewares. n 10-24

  25. Polyacrylonitrile High strength. Good resistance to moisture and solvents. Applications: sweaters and blankets. Commoner for SAN and ABS resins. SAN Random amorphous copolymer of styrene and acrylonitrile. Better chemical resistance, high heat deflection temperature, toughness and load bearing characteristics than polyester alone. Applications: Automotive instrument lenses, dash components, knobs, blender and mixer bowls. Polyacrylonitrile and Styrene-Acrylonitrile (SAN) H H C C H C N Does not Melt. n 10-25

  26. ABS • ABS = Acrylonitrile + Butadiene + Styrene (Three monomers). • Applications: Pipe and fittings, automotive parts, computer and telephone housings etc. Table 7.4 Figure 7.31 10-26 After G. E Teer, ABS and Related Multipolymers, in Modern Plastics Encyclopedia,” McGraw-Hill, 1981- 1982.

  27. Polymethyl Methacrylate (PMMA) • An acrylic commonly known as Plexiglas. • Applications: Glazing of aircraft, boats, skylights, advertising signs etc. H CH3 C C H C • Rigid and relatively strong. • Completely amorphous and • very transparent. O CH3 n 10-27

  28. Fluoroplastics • Monomers have one or more atoms of fluorine. • Polytetrafluoroethylene(PTFE): • Applications: Chemically resistant pipe, parts, molded electrical components, nonstick coating etc. F F C C F F • Exceptionally resistant to • chemicals. • Useful mechanical properties • at a wide temperature range. • High impact strength but low • tensile strength. • Good wear and creep resistance. Melting Point 1700C n 10-28

  29. Polychlorotrifluroethylene (PCTFE) Applications: Gaskets, chemical processing equipments, seals and electric components. F F C C F Cl Melting Point 2180C • Chlorine atom substitutes • for every fourth fluorine atom. • Can be extruded and mold • easily. n 10-29

  30. Engineering Thermoplastics • Low density, low tensile strength. • High insulation, good corrosion resistance. Table 7.5 10-30

  31. Polyamides (Nylons) • Main chain structure incorporates repeating amide group. • Processed by injection molding. • Examples: O H C N Amide linkage 10-31

  32. Properties of Nylon • High strength due to hydrogen bonding between molecular chain. • Flexibility of carbon chain contributes to molecular flexibility, low melt viscosity and high lubricity. • Applications: Electrical equipments, gears, auto parts, packaging etc. Figure 7.35 10-32 After M. I. Kohan(ed.), “Nylon Plastics,” Wiley, 1983, p.274

  33. Polycarbonate • Applications: Precision parts, cams, gears, helmets, power tool housings and computer terminals. • High strength, toughness and • dimensional stability. • Very high impact strength. • high heat deflection • temperature. • Resistance to corrosion. 10-33

  34. Phenyl Oxide Based Resins • Produced by oxidative coupling of phenolic monomers. • Applications: Electric connectors, TV tuners, small machine housing, dashboards and grills. • High rigidity, strength, chemical resistance, dimensional stability and heat deflection temperature. • Wide temperature range, low creep • High modulus. 10-34

  35. Acetals • Strongest (68.9 Mpa) and stiffest (2820 Mpa) thermoplastics. • Homopolymer is harder and rigid than copolymer. • Low wear and friction but flammable. • Applications: Fuel systems, seat belts, window handles of automobiles, couplings, impellers, gears and housing. • 2 Types • Homopolymers • Copolymers H C O H Polyoxymethylene mp: 1750C • Excellent long term load carrying capacity • and dimensional stability. n 10-35

  36. Thermoplastic Polyesters Good insulator: independent of temperature and humidity. • Applications: Switches, relays, TV tuner components, circuit boards, impellers, housing and handles. • Phenylene ring provides rigidity. • Good strength and resistant to most chemicals. 10-36

  37. Polysulfone and Polyphenylene Sulfide. • Polysulfone:Phenylene ring provides high strength and rigidity. • Applications: Electrical connectors, cores, circuit boards, pollution control equipments. • Polyphenylene Sulfide:- • Rigid and strong. • Highly crystalline. • No chemical can dissolve it below 2000C. • Applications: Chemical process equipment, emission control equipment, electrical connectors. • Can be used for long time • at high temperature. Mp: 2880C S n 10-37

  38. Polyetherimide and Polymer Alloys • Polyetherimide: • High heat and creep resistance and rigidity. • Good electric insulation. • Applications: High voltage circuit breaker housing, coils etc. • Polymer alloys: Mixture of structurally different homopolymers or copolymers optimizes properties. • Some degree of compatibility needed. • Example:- Bayblend MC2500 (ABS/Polycarbonate) 10-38

  39. Thermosetting Plastics • High thermal and dimensional stability, rigidity, resistance to creep, light weight. Table 7.7 10-39 Source: Materials Engineering, May 1972.

  40. Phenolics • Low cost, good insulating and mechanical properties. • Produced by polymerization of phenol and formaldehyde. • General purpose compounds: Usually wood flour filled to increase impact resistance. • High impact strength compounds: Filled with cellulose and glass fibers. • High electrical insulating compounds: Mineral (Mica) filled. • Heat resistant compounds: Mineral filled. • Applications: Wiring devices, auto transmission parts, plywood lamination, adhesives, shell molding. 10-40

  41. Epoxy Resins • Good adhesion, chemical resistance and mechanical properties. • High molecular mobility, low shrinkage during hardening. • Applications: Protective and decorative coating, drum lining, high voltage insulators and laminates. O CH2 C H Epoxide group 10-41

  42. Unsaturated Polyesters • Low viscosity and can be reinforced with low viscosity materials. • Open mold lay up or spray up techniques are used to process many small parts. • Compression molding is used for big parts. • Applications: Automobile panels and body parts, boat hulls, pipes, tanks etc. • Have reactive double • Carbon-Carbon covalent • bonds. 10-42

  43. Amino Resins (Ureas and Melamines) • Formed by reaction of formaldehydes with compounds having –NH2 group. • Combined with cellulose fillers to produce low cost products with good mechanical properties. • Applications: Electrical wall plates, molded dinnerware, buttons, control buttons, knobs, flooring etc. 10-43

  44. Elastomers (Rubbers) • Natural rubber: Produced from latex of Havea Brasiliensis tree. • Vulcanization: Heating rubber with sulfur and lead carbonate. • Increases tensile strength. • Restricts molecular movement by crosslinking of molecules. H CH3 H H C C C C H H n Figure 7.41 10-44

  45. Natural Rubber - Properties Table 7.8 Figure 7.43 10-45 After M. Eisenstadt, “Introduction to Mechanical properties of Materials,” Macmillan, 1971, p.89.

  46. Synthetic Rubbers • Styrene-Butadiene rubber (SBR): Most widely used. • Greater elasticity than natural rubbers. • Tougher and stronger, war resistant. • Absorbs organic solvents and swell. • Nitrile Rubbers: 55-82% Butadiene and 45-18% acrylonitrile. • Resistance to solvents and wear. Less flexible. • Polychloroprene: Increased resistance to oxygen, ozone, heat and weather. • Low temperature flexibility, high cost. Figure 7.44 H Cl H H C C C C H H n 10-46

  47. Vulcanization of Polychloroprene Elastomers • Silicone Rubbers: • Wide temperature range. • Used in gaskets, electric insulation etc. 2ZnCl2 + MgO OH 2Zn + MgCl Cl H2O X Si O X CH3 Si O CH3 Example n n 10-47

  48. Deformation of Thermoplastics • Below Tg Elastic deformation. Above Tg Plastic deformation. Elastic deformation Elastic or plastic deformation Plastic deformation Figure 7.46 Figure 7.45 After T. Alfrey, “mechanical Behavior of Polymers,” Wiley-Interscience, 1967. After M. Eisenstadt, “Introduction to Mechanical properties of Materials,” Macmillan, 1971,p.264. 10-48

  49. Strengthening of Thermoplastics • Increasing average molecular mass increases strength upto a certain critical mass. • Degree of crystallinity increases strength, modulus of elasticity and density. • Chain slippage during permanent deformation can be hindered by introduction of pendant atomic groups to main carbon chain. • Strength can be increased by bonding highly polar atoms on the main carbon chain. 10-49

  50. Strengthening of Thermoplastics (Cont..) • Strength can be increased by introduction of oxygen and nitrogen atoms into main carbon chain. • Introduction of phenylene ring into main polymer chain with other elements increases strength. • Adding plastic fibers increases the strength. • Thermosetting plastics can be strengthened by reinforcements and creation of covalent bonds by chemical reaction during setting. Figure 7.49 10-50 After J. A. Sauer and K. D. Pae, in “Introductin to Polymer Science and Technology,” Wiley, 1977, p.331.