Band gap variations in ferritin-templated nanocrystals

Band gap variations in ferritin-templated nanocrystals. John S. Colton Physics Department Brigham Young University. Collaborators: Stephen Erickson (next talk) Dr. Richard Watt (BYU Chemistry) Trevor Smith (BYU Chemistry). Talk for APS March Meeting Mar 5, 2014.

tsears
Télécharger la présentation

Band gap variations in ferritin-templated nanocrystals

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Band gap variations in ferritin-templated nanocrystals John S. Colton Physics Department Brigham Young University Collaborators: Stephen Erickson (next talk) Dr. Richard Watt (BYU Chemistry) Trevor Smith (BYU Chemistry) Talk for APS March Meeting Mar 5, 2014 Reference for some of this: Colton et al., Nanotech. 25 (2014) 135703

  2. What is ferritin? “3-fold channel”

  3. 1. Nanocrystal Why is ferritin interesting? • Template for nanocrystals • Photo-oxidation catalyst • Self healing against photo corrosion From Watt, Petrucci, and Smith, Catl. Sci. Technol. 2013

  4. Why is ferritin interesting? (cont.) • Surface bonding

  5. Nanocrystals grown with ferritin • From Watt, Petrucci, and Smith, Catl. Sci. Technol. 2013

  6. Examples of our samples Non-native samples • Take iron out: dithionite dialysis, 0.050 M TRIS-base buffer at pH 7.4 carefully titrated with NaNO3. • Putting iron (for example) back in: 10 mM ferrous ammonium sulfate added at a rate of 200 irons per ferritin every 10 minutes Manganese replacing iron Native

  7. Ferrihydrite basics • (Fe3+)2O3 • 0.5H2O • Nanomaterial • Found in soils • Found in organisms • Contains defects image: Wikipedia Lopez-Castro et al., Dalton Trans. 2012

  8. Nanocrystals grown with ferritin • From Watt, Petrucci, and Smith, Catl. Sci. Technol. 2013 1.0 – 3.5 eV

  9. (1967) (1955) Absorption to measure band gaps • Figures from Yu and Cardona, Fundamentals of Semiconductors (2010)

  10. Band structure of ferrihydrite in native ferritin • Figure from Colton et al, Nanotechnology (2014) • Compare table value: 2.5-3.5 eV, More details: next talk • ~1100 iron atoms per ferritin

  11. Reconstituted ferritin: 1500 Fe atoms/ferritin • band gap vs. day • Tris buffer native ferritin

  12. Band gap vs. day • 1500 Fe atoms/ferritin • characteristic 1/e time in Tris: 10.9 days TRIS buffer, two-line Imidizole buffer, six-line

  13. Band gap vs. day, cont. TRIS buffer 10.9 days two-line Imidizole buffer Instantaneous six-line TEM studies: coming soon

  14. Nanocrystals grown with ferritin • From Watt, Petrucci, and Smith, Catl. Sci. Technol. 2013

  15. Band gap of other metal oxides • Imidizole buffer • Compare: “CoOOH 1.4-1.8 eV” from table • Size dependent effects: next talk

  16. Conclusions • Ferritin: template for nanocrystal growth • with many other desirable properties • Indirect band gap / direct transition • FeOOH: 1.92 eV / 3.05 eV • CoOOH: 1.59 eV / 2.74 eV • MnOOH: 1.54 eV / 2.59 eV • Mineralization • 10.9 days (in Tris) • nearly immediate (in imidizole) Reference for some of this: Colton et al., Nanotech. 25 (2014) 135703