An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Flux pinning in general Adrian Crisan School of Metallurgy and Materials, University of Birmingham, UK and National Institute of Materials Physics, Bucharest, Romania

  2. CONTENTS • Introduction: type I vs. type II • Vortices • Pinning • Bulk Pinning Force Density • Pinning Potential

  3. INTRODUCTION: Type I vs. Type II Type I superconductors • They cannot be penetrated by magnetic flux lines (complete Meissner effect) • They have only a single critical field at which the material ceases to superconduct, becoming resistive • They are usually elementary metals, such as aluminium, mercury, lead

  4. Type II superconductors • Gradual transition from superconducting to normal with an increasing magnetic field • Typically they superconduct at higher temperatures and fields than Type I • Between Meissner and normal state there is a large “mixed” or “vortex” state • They have two critical fields (upper and lower) • They are ussually metal alloys, intermetallic compounds, complex oxides (e.g., Cu-based HTSC) and, recently discovered, pnictides and chalcogenides

  5. Phase diagram of “classical” superconductors

  6. Penetration depth (l) • Diamagnetic material (no internal flux) • Currents to repel external flux confined to surface • Surface currents must flow in finite thickness (penetration depthl)

  7. Coherence length (x) • characterises the distance over which the superconducting wave function y(r) can vary without undue energy increase • the distance over which the superconducting carriers concentration decreases by Euler’s number e • GL parameter k=l/x; if k<1/21/2 then Type I; k>1/21/2 then Type II

  8. II. VORTICES Vortex (mixed) state • Normal regions thread through superconductor - Ratio between surface and volume of the normal phase is maximised • Cylinders of normal material parallel to the applied field (normal cores) • Cores arranged in regular pattern to minimize repulsion between cores (close-packed hexagonal lattice) – flux lattice

  9. Flux quanta - vortex

  10. Phase diagram of High-Tc superconductors and Vortex Melting Lines • The vortex lattice undergoes a first-order melting transition transforming the vortex solid into a vortex liquid [Fisher et al, PRB 43,130, 1991]. • For high anisotropy, at low magnetic fields (approx 1 Oe in BSCCO [A.C. et al, SuST 24, 115001, 2011), there is a reentrance of the melting line [Blatter et al, PRB 54, 72, 1996]. • The flux lines in the vortex -liquid are entangled resulting in an ohmic longitudinal response, hence the vortex liquid and normal metallic phases are separated by a crossover at Hc2. • For low enough currents • VL- linear dissipation: E ≈ J • VS (VGlass)- strongly nonlinear dissipation: E ≈ exp[-(JT/J)m]

  11. III. PINNING Lorenz force (FL) and pinning force (Fp) In the presence of a magnetic field perpendicular to the current direction, a Lorentz force FL = j ×f0, where j is the current and f0 is the magnetic flux quantum, acts on the vortices • If FL is smaller than the pinning force Fp, vortices do not move. Columnar defects Point defects Defect-free sample

  12. Dimensionality and strength of PCs

  13. IV. BULK PINNING FORCE DENSITY • FP determined from magnetization loops M(Ha) Fp=BxJc Jc=Ct.DM (thin films; m=DM/2; d-thickness; a,b-rectangle dim.)

  14. Dew-Hughes model F = Fp/Fpmax = hp(1-hq) ; h = B/Birr p and q depend on the types of pinning centres. • Classified by the number of dimensions that are large compared with the inter-flux-line spacing; and • by the type of the core: “Dk pinning” and “normal pinning” Ususlly there are several types of pinning centres. F = Ahp1(1-hq1)+Bhp2(1-hq2)+Chp3(1-hq3)+....... D. Dew-Hughes, Philosophical Magazine 30 (1974) 293

  15. Volume normal; (1-h)2, no max; F=1 Surface n; h1/2(1-h)2 ; max at 0.2, Fm=0.286, B= 3.5 Volume Dk; h(1-h) , max at 0.5, Fm=0.25, A=4 Surface Dk; h3/2(1-h) ; max at 0.6, Fmax=0.186, C=5.37

  16. Point n; h(1-h)2; max at 0.33, Fmax=0.148, D=6.76 Point Dk; h2(1-h) ; max at 0.67, Fmax=0.148; E=6.76

  17. V. PINNING POTENTIAL • Energy needed by the flux line to escape from the potential well crated by the pinning centre • Shape and influence on superconducting properties modelled in several ways, depending on material, strength and distribution of pinning centres • In 1962 Anderson predicted that movement of vortices with a drift velocity v will create dissipation (electric field) E=Bxv

  18. Dissipation occurs through two mechanisms: • 1. Dipolar currents which surround each moving flux line (eddy currents) and which have to pass through “normal conducting vortex core” • 2. Retarded relaxation of the order parameter when vortex core moves • Anderson and Kim predicted that thermal depinning of flux lines can occur at finite temperatures T (“flux creep”).

  19. Anderson-Kim model • Model assumes that flux creep occurs due to thermally-activated jump of isolated bundles of flux lines between two adjacent pinning centres. • The jump is correlated for a bundle of vortices of volume (correlated volume), Vc due to the interactions between them • In the absence of transport current (i.e., no Lorentz force) the bundle is placed in a rectangular potential well of height Uo. • Due to thermal energy, there are jumps over the barier with a frequency = oexp(-Uo/kT)

  20. (3) (2) (1) (1) (2) (3) (1): I=0 (2): 0<I<Io (3): I=Io Second term is ussualy neglected, since current densities of interest are smaller than J0 Critical current density is defined arbitrarily at a certain electric field, e.g., 10-6 V/cm. It follows:

  21. Logarithmic decay, magnetic relaxation J; M (a.u.) ln (t) K-A model: -pinning potential decreases linearly with current -remnant magnetization and persistent current (or critical current density) decay logarithmically with time

  22. Modified Anderson-Kim model • Tilted-washboard cosine potential, which leads to U=U0[1-(J/Jc)]3/2 • The two forms can be generalized as U=U0[1-(J/Jc)] • Such forms focus on the detailed behavior near Jc, which is appropriate for the classic superconductors where fluctuation effects cause only slight degradation of Jc

  23. Larkin-Ovchinnikov collective pinning model • Cooperative aspects of vortex dynamics • Formation of vortex lattice will be a result of a competition between: -vortex-vortex interaction, which tends to place a vortex on a lattice point of a periodic hexagonal/triangular lattice; and - vortex-pin interaction, which tends to place a vortex on the local minimum of the pinning potential • v-v interaction promotes global translational invariant order • v-p interaction tend to suppress such long-range order, if pinning potential varies randomly

  24. Long-range order of an Abrikosov lattice is destroyed by a random pinning potential, no matter how weak it is. • Periodic arrangement is preserved only in a small corellated volume vc which depends on the strength of the pinning potential and the elasticity of the vortex lines • Correlated volume vc increase strongly with decreasing current density J, which leads to a power-law dependence of effective pinning potential on the current density

  25. The above dependence leads to a non-ohmic current-voltage characteristic of the form: In an inductive circuit, V is proportional to dJ/dt T010-6 s

  26. Zeldov effective pinning • Magneto-resistivity and I-V curves of YBCO films • Potential well having a cone-like structure exhibiting a cusp at its minimum and a broad logarithmic decay with the distance E. Zeldov et al, PRL 62, (1989) 3093 , PRL .56, (1990) 680 A.C. et al, SuST 22, 045014, 2009