NCHRP Projects 9-25 & 9-31: Findings Related to Surface Cracking

NCHRP Projects 9-25 & 9-31: Findings Related to Surface Cracking. FHWA Mixture ETG Washington, DC February 2003. Advanced Asphalt Technologies, LLC. “Engineering Services for the Asphalt Industry”. Fatigue Testing and Analysis. Continuum damage approach

annot
Télécharger la présentation

NCHRP Projects 9-25 & 9-31: Findings Related to Surface Cracking

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. NCHRP Projects 9-25 & 9-31:Findings Related to Surface Cracking FHWA Mixture ETG Washington, DC February 2003 Advanced Asphalt Technologies, LLC “Engineering Services for the Asphalt Industry”

  2. Fatigue Testing and Analysis • Continuum damage approach • Normalization to reduce or eliminate effect of mixture stiffness • Produces single continuum damage fatigue constant “C**2” characteristic of intrinsic fatigue resistance • Independent of stress- vs. strain-control

  3. Effective Binder Content

  4. WesTrack Cracking Vs. Vbe

  5. Mixture Stiffness • Increased mixture stiffness decreases strains • Decreased strains increases fatigue life • HOWEVER…

  6. Binder Viscosity & Healing • Healing more rapid with low viscosity binders • Generally, fatigue resistance will decrease with increased high-temperature binder grade

  7. Healing and Binder Viscosity(after Little et al., 1999)

  8. Age Hardening |G*|aged / |G*|unaged = 1.76  0.0037(% LS) + 0.028 (VTM)  0.068 (Agg. S.A.) R2 = 74 %

  9. Age Hardening:Aggregate Type and Permeability • Limestone fines appears to significantly retard age hardening • Age-hardening also decreases with decreasing permeability • Increasing aggregate surface area • Decreasing air voids

  10. Summary: Factors Affecting Fatigue Cracking • Effective binder content • Structural stiffness • Mixture stiffness • Binder viscosity & healing • Mixture age hardening

  11. Ways to Increase Fatigue Life • Increase binder content • Decrease binder viscosity • Increase pavement thickness • Use limestone/hydrated lime fines and/or filler

  12. Controlling Rut Resistance • Rut resistance a function of • Binder grade • N-design • VMA relative to aggregate fineness • To maintain rut resistance with increased binder, increase proportion of fines/mineral filler

  13. Mix Resistivity

  14. Recommendations • Use 9.5 and 12.5-mm mixtures for wearing courses • Increase binder 0.5 % by weight • Maintain filler/binder ratio • Avoid unnecessary grade bumping • Use limestone/hydrated lime fines and mineral filler

  15. What Can 0.5 % Change in Binder Content Do?