TEM and XSTM Characterization of Embedded InAs Quantum Dots

Department of Materials Science & Engineering University of California at Berkeley. TEM and XSTM Characterization of Embedded InAs Quantum Dots. Matt Lowry Presented for NSEC203/EEC235 April 16, 2008. Department of Materials Science & Engineering University of California at Berkeley.

emilia
Télécharger la présentation

TEM and XSTM Characterization of Embedded InAs Quantum Dots

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Department of Materials Science & Engineering University of California at Berkeley TEM and XSTM Characterization of Embedded InAs Quantum Dots Matt Lowry Presented for NSEC203/EEC235 April 16, 2008

  2. Department of Materials Science & Engineering University of California at Berkeley Motivation • Optical & electrical properties depend on shape, size, composition, and symmetry • AFM vs. XSTM vs. TEM • Changes due to capping • In segregation • TEM averaging effects • XSTM cleavage planes • Optimize growth strategies for potential applications • Good microscopy is difficult

  3. Department of Materials Science & Engineering University of California at Berkeley Cross-Sectional Scanning Tunneling Microscopy (XSTM) • Raster tip • I ~ exp (-kz) • Image or topography • http://www.insp.upmc.fr/axe1/Dispositifs%20quantiques/AxeI2_more/PRINCIPLE/STSprin.HTM

  4. Department of Materials Science & Engineering University of California at Berkeley Shape and Size Determination • Full and truncated pyramidal quantum dots • Cleaved on (110) planes • Only model 2 was observed • D.M. Bruls, et al., Appl. Phys. Lett. 81, 1708 (2002).

  5. Department of Materials Science & Engineering University of California at Berkeley Composition Determination • Stress relaxes on free surface due to 7% lattice mismatch • InxGa1-xAs alloy with linear In gradient • 60%-100% In gradient from bottom to top • Lattice constant • Increase of 35pm across dot due to In content increase • D.M. Bruls, et al., Appl. Phys. Lett. 81, 1708 (2002).

  6. Department of Materials Science & Engineering University of California at Berkeley Multi-Directional Analysis of an Isolated Quantum Dot • Multi-directional analysis to detect asymmetries • Splitting of exciton states • InAs dot with GaAs cap • Focused Ion Beam used to isolate a quantum dot in a micropillar • 80nm X 80nm pillar with 5nm amorphous region T. Kita, et al., Appl. Phys. Lett. 90, 041911 (2007).

  7. Department of Materials Science & Engineering University of California at Berkeley TEM of an Isolated Quantum Dot • Along [110] : 21nm Along [-110] : 23nm • Anisotropic growth due to faceting • Preferential strain in [-110] • Asymmetry of diffraction patterns T. Kita, et al., Appl. Phys. Lett. 90, 041911 (2007). [110] Zone Axis [-110] Zone Axis

  8. Department of Materials Science & Engineering University of California at Berkeley Conclusions • Cross-sectional STM has allowed for the determination of shape, size, and composition of InAs quantum dots embedded in GaAs. • A combined FIB/TEM approach has allowed for the determination of asymmetric crystal strain in an isolated InAs quantum dot embedded in GaAs. • Both procedures are applicable to other systems • Better characterization will hopefully aid in fulfilling the promise of applications