Bulk Resistivity measurement of Phenolic

Bulk Resistivity measurement of Phenolic. Liang Guan. >> Method >> New measurement on Sample Batch4-T1. 06/06/2011 Bi-weekly TGRPC R&D Meeting . Bulk Resistivity measurement-Method (1) . GND. 9(3×3)/25(5×5) points sampling . pA. Electrode A ( ø=5cm). 12. 15. 13. 14. 11. 25.

gerald
Télécharger la présentation

Bulk Resistivity measurement of Phenolic

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Bulk Resistivity measurement of Phenolic Liang Guan >> Method >> New measurement on Sample Batch4-T1 06/06/2011Bi-weekly TGRPC R&D Meeting

  2. Bulk Resistivity measurement-Method (1) GND • 9(3×3)/25(5×5) points sampling pA Electrode A (ø=5cm) 12 15 13 14 11 25 23 24 22 21 3atm Pressure is applied (CMS) 32 35 33 34 31 41 42 45 43 44 55 53 54 51 52 Specimen (Size: 40cm*40cm Thickness:1mm) Conductive rubber (thickness: 0.5-1mm) * rubber filled with small conductive metal or carbon spheres Electrode B (ø=8cm) +500V 1

  3. Bulk Resistivity measurement-Method (1) 高压（高压电缆中心线） 高压电源 高压电缆 1kΩ,10kΩ,100kΩ,1MΩ 地线 （高压电缆外包皮） 数字万用表（电压模式） 2

  4. Bulk Resistivity measurement-Method (3) • Assume Effective area • Sample bulk resistivity on the order of 108Ω·cm/109Ω·cmand thickness of 1 mm • For HV=500V, current flowing through sample ~1000μA/100μA V Multi-meter • Voltage scale on Rt Rs Rt 500V 3

  5. Logbook • Specify the sample ID, charging time, RH, Temperature etc. Preliminary 4

  6. Bulk resistivity of Batch 4-T1 sample >116hours 5

  7. Bulk resistivity of Batch 4-T1 sample • Measured resistivity is on the order of 109 Ohm.cm at Room temperature  similar to the value measured 2 weeks ago but still a factor of two higher than the value measured 2 months ago when the sample just arrived. • Bulk resistivity value of the sample Batch4-T1 shows some correlation with the temperature • lower temperature results in higher resistivity • resistivity value @ ~25C slightly increasing during one week test (RH<40%)

  8. Material study - Prof. Changguo Lu’s study • Surface condition: defects such as pins, hole, ridge etc. present on the inner surface of Bakelite will make shape electric field thus increasing the noise rate • UV absorption • Ageing: HF acid chemical active ATLAS RPC C4H10 5% SF6 0.3% C2H2F2 94.7% CMS RPC C4H10 3.5% SF6 0.3% C2H2F2 96.2% • Significantly reduce resistivity • surface smoothness - Water : Help to slow down the decrease of resistivity but also help to form HF