ANALISI DI MATERIALI CON FASCI IONICI ALL’ACCELERATORE DI FIRENZE Massimo Chiari

ANALISI DI MATERIALI CON FASCI IONICI ALL’ACCELERATORE DI FIRENZE Massimo Chiari. Fisica Sperimentale (I.N.F.N.). Dipartimento di Fisica. PIXE-induced XRF. multi-angle scattering chamber. multipurpose IBA vacuum chamber. FACILITY AMS/IBA DI FIRENZE. da costruire. da montare.

kyra-wilson
Télécharger la présentation

ANALISI DI MATERIALI CON FASCI IONICI ALL’ACCELERATORE DI FIRENZE Massimo Chiari

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. ANALISI DI MATERIALI CON FASCI IONICI ALL’ACCELERATORE DI FIRENZE Massimo Chiari

  2. Fisica Sperimentale(I.N.F.N.) Dipartimento di Fisica

  3. PIXE-induced XRF multi-angle scattering chamber multipurpose IBA vacuum chamber FACILITY AMS/IBA DI FIRENZE da costruire da montare external beam for aerosol analysis già operativi external m-beam Tandetron Accelerator 3 MV terminal voltage electrostatic chopper IBA Dual source injector external beam for archaeometry Multi-sample AMS injector High-energy AMS spectrometer

  4. TECNICHE DI ANALISICON FASCI IONICI camera di scattering bersaglio beamline acceleratore protoni radiazione caratteristica rivelatore segnale spettro di energia

  5. PRINCIPALI TECNICHE IBA PIXE (Particle Induced X-ray Emission) PIGE(Particle Induced g -ray Emission) PESA(Particle Elastic Scattering Analysis)

  6. E(keV) VANTAGGI E LIMITI DELLE TECNICHE IBA multielementali alta sensibilità analisi quantitative non sono necessari pretrattamenti dei campioni non distruttive capacità di scanning capacità di microanalisi analisi superficiali nessuna informazione sui legami chimici

  7. Si (Li) “BIG” Collimatore FC Target Si (Li) “SMALL” Finestra Upilex (7.5mm) He 1 cm

  8. TEST DI RISOLUZIONE SPAZIALE in esterno(0.1 mm Si3N4 + 2 mm He) in vuoto 125 mm scansione su griglia di rame, di passo 125 mm FWHM ~5 mm FWHM ~10 mm

  9. APPLICAZIONI IN GEOLOGIA Immagine ottica Inclusioni Mg Al 830 mm Si Ti Ca Fe Fe 830 mm Max Min

  10. Area selezionata SMALL X BIG 370mm

  11. APPLICAZIONI IN GEOLOGIA Th Y Si Ce Sr Al 750 mm

  12. C N He O Cr MICRO-PESA IN ESTERNO 3 MeV pq = 135° Cr 46 mg cm-2/ Mylar 6 mm

  13. SIAMO DISPONIBILI PER EVENTUALI PROPOSTE DI ESPERIMENTI ?

  14. m M Ei M m  Ef m = 1 O rivelatore N C H PARTICLE ELASTIC SCATTERING ANALYSIS DE maggiori per piccoli m (nuclei leggeri) DE maggiori per grandi  (backscattering) M  m  solo scattering in avanti