Characterisation of porous materials using Electron Microscopy

Characterisation of porous materials using Electron Microscopy. Dr. Patricia J. Kooyman DelftChemTech / National Centre for HREM Delft University of Technology p.j.kooyman@tudelft.nl. Bulk (structural) information. Transmission Electron Microscopy (TEM). Surface information.

william-garza
Télécharger la présentation

Characterisation of porous materials using Electron Microscopy

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Characterisation ofporous materials usingElectron Microscopy Dr. Patricia J. Kooyman DelftChemTech / National Centre for HREM Delft University of Technology p.j.kooyman@tudelft.nl

  2. Bulk (structural) information Transmission Electron Microscopy (TEM) Surface information Scanning techniques Scanning probe microscopy: STM, AFM Scanning Electron Microscopy (SEM)

  3. ElectronMicroscopyTechniques

  4. What is TEM? • A technique using high-energy electrons to obtain a 2D projection of a 3D structure. • The highest possible resolution is currently about 0.1 nm.

  5. Electron-solid interactions TEM EDX Specimen Element Elastically specific X-rays scattered Secondary electrons electrons ED / HREM Visible light Incident electrons Direct beam Backscattered SEM Inelastically electrons scattered Auger electrons electrons EELS

  6. The SEM

  7. SEMTEM particle morphology(particle morphology) surface morphology2D projection - internal structure elemental analysis elemental analysis 5 nm - 500 micron1 nm - 5 micron electr backscatter diffr electron diffraction EELS

  8. General features of SEM • Electrons interact with specimen • High vacuum necessary • Specimen should be conducting (sputter with Au) • Particle morphology • Surface imaging • Elemental analysis • Resolution ~ 1 nm

  9. General features of TEM • Electrons interact with specimen • High vacuum necessary (~ 10-7 Torr for HREM) • Specimen should be very thin (< 10 nm for HREM) • 2D projection of 3D structure • Structural analysis • Elemental analysis • Resolution ~0.1 nm

  10. Optical systems http://www.vcbio.sci.kun.nl/fesem/info/

  11. Optical system of a TEM specimen focus plane for diffraction intermediate 1 focus plane for image image cross-section TEM intermediate 2 final image imaging diffraction

  12. Electron diffraction (TEM) MFI HR bright-field image ED pattern Fourier transform

  13. Electron backscatter diffraction(EBSD - SEM) High quality EBSD pattern

  14. Electron backscatter diffraction (EBSD - SEM) MFI SEM image Stavinski et al. Angew. Chem. 120 (2008) 5719 EBSD patterns spots A and D Indexed EBSD patterns spots A and D

  15. TEM imaging centered dark field HREM bright field dark field

  16. Ru/aluminaSoede, DUT Bright field image

  17. d-spacing Ru/aluminaSoede, DUT Electron Diffraction Pattern

  18. Dark field image with Ru-diffracted beam Bright field image Ru/alumina Soede DUT

  19. TEM - information obtained • Method Information • * bright-field * microstructural • imaging nb: 2D info of 3D • * high resolution structure! • imaging * electron diffraction * crystallographic pattern (cf XRD) * generated X-rays *elemental analysis (EDX)

  20. Sample preparationpowders / suspensions / sols

  21. Samplepreparationpowders / suspensions / sols

  22. Sample preparation: crushing suspension in eg ethanol crush deposit on grid with carbon film 3 mm

  23. Microgrid carbon film Quantifoil

  24. MOF on microgrid carbon film Gascon, TUD

  25. TEM Fe-MFI Taboada, TUD

  26. SEM of same sample

  27. Samplepreparationone-piece samples

  28. Samplepreparationone-piece samples

  29. Sample preparation: ion milling specimen polishing holder polishing 5-10 micron thick Ar ion beams

  30. Sample preparation: ultramicrotomy catalyst core slices < 50 nm glue mantle diamond knife slices on grid water bath also possible at liquid nitrogen temperature

  31. Ultramicrotomy powder specimen ultramicrotomed specimen

  32. MCM-41 mesoporous zeotype material pore size > 3 nm possibility to convert larger molecules different phases are found

  33. MCM-41

  34. HPA/MCM-41 fresh Verhoef, TUD Ordered Disordered

  35. HPA/MCM-41 used

  36. HPA/MCM-41 XRD patterns

  37. Fe-Si-SBA-15: TEM Li, Hensen, TU/e J. Phys. Chem. B 110 (2006) 26114 -26121

  38. Fe-Si-SBA-15: EDX

  39. Pt-Rh/alumina (Grisel, UL) Particle size distribution? Alloying? Use TEM/HREM in combination with EDX

  40. overview cluster Pt-Rh/alumina (Grisel, UL)

  41. full scale enlarged scale Pt-Rh/alumina (Grisel, UL)

  42. optimal imaging zeolite 5 degree tilt zeolite amorphised Pt/zeolite

  43. TiO2 in TUD-1 Hamdy-Saad, TUD Peeters, TUE

  44. 3D TEM Reconstruct 3D structure from tilt series at different angles of the same area of material “Electron Tomography”

  45. 3D TEM Procedure: Acquire tilt series of a particle from +70 to -70 degrees at 1 or 2 degrees steps Recombine these images to 3D reconstruction Depict as slices through the particle or as volume rendering

  46. 2D TEM - loss of information

  47. 3D TEM - cycle

  48. 3D TEM - result Single image from series Slice of reconstruction Jansen et al., Utrecht University

  49. New mesoporous mat: SEM

  50. New mesoporous mat: TEM MSU-3 Prouzet et al., J.Mater.Chem. 12 (2002) 1553