Organic Molecules on Insulating Surfaces Investigated by NC-AFM

Organic Molecules on Insulating Surfaces Investigated by NC-AFM. February 26 th , 200 4 MPI Dresden , Germany. Enrico Gnecco Institute of Physics University of Basel, Switzerland. metallic substrate. Motivations. I. molecule. electrodes. Chemistry is important!.

enid
Télécharger la présentation

Organic Molecules on Insulating Surfaces Investigated by NC-AFM

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Organic Molecules on Insulating Surfaces Investigated by NC-AFM February 26th, 2004 MPI Dresden, Germany • Enrico Gnecco • Institute of Physics • University of Basel, Switzerland

  2. metallic substrate Motivations I molecule electrodes

  3. Chemistry is important! The circuit architecture still remains a problem ! Motivations • Advantage: • Insulating spacers (porphyrins, landers) I molecule electrodes metallic substrate • Disadvantage: • Spacers adaptation to the substrate  changes in the electronic properties  Insulating surfacesare potentially good candidates

  4. UHV atomic force microscope • Surface preparation in vacuum • Light-beam adjusted by motorized mirrors L. Howald et al., APL 63 (1993) 117

  5. Cu-tetra porphyrin (Cu-TBPP) on Cu(100): STM NC-AFM Observing organic molecules with AFM:intrinsic problems • The vertical resolution is ~ the same but... • Long range contribution is detrimental for lateral resolution • The tip sharpness is critical

  6. different interaction potentials  different set points ! Observing organic molecules with AFM:intrinsic problems

  7. Comparing force-distance curves: • (i) on the molecule legs and • (ii) on the substrate:  Switching energy: W ~ 0.3 eV Ch. Loppacher et al., Phys. Rev. Lett. 90, 066107 (2003) Despite the problems... • Energetics of a single molecule can be studied:

  8. Stable nanopatterns can be created: E. Gnecco et al., Phys. Rev. Lett. 88, 215501 (2002) Switching to insulators... • “Atomic” resolution on KBr(100): a = 0.66 nm b = 0.47 nm 5 nm 50 nm

  9. Heating at 380 °C  Spiral pattern Step height: 0.35 nm K. Yamamoto et al., J. Cryst. Growth 94 (1989) 629 Trapping the molecules... • How to reduce the mobility of the molecules?

  10. ~ 1.5 nm ~ 3.3 nm • Multi-layered structures L. Nony et al., Nanotechnology 15 (2004) 591 Cu-TBPP on KBr(100) • ½ ML on KBr(100) at room temperature: • The steps are decorated by “molecular wires” • No evidence of internal structures  The mobility of the molecules is still high

  11. R. Bennewitz et al., Surf. Sci. 474, L197 (2001) Lowering the mobility... • KBr(100) irradiated with 1 kV e- at 120 °C: • Rectangular holes (~10 nm wide) • Mono-layer depth (0.33 nm) Holes as molecular traps?

  12. Perylene tetracarboxylic dianhydride (PTCDA): topography 140 nm damping “Legless” molecules in the holes • The holes are empty or (partially) filled • No resolution of single molecules

  13. Molecules with large dipole moment: Sub-phtalocyanine (SubPc) d = 4.8 debye S. Berner et al., Phys. Rev. B 68 (2003) 115410 Towards polar molecules... • Three fold symmetry • Charge of the chlorine: 0.42 e

  14. 18 nm • Single molecules are resolved ! L. Nony, E. Gnecco, R. Bennewitz, A. Baratoff, and E. Meyer et al., in preparation SubPC molecules on e--irradiated KBr • 1 ML on KBr(100) at 80 °C:

  15. 1.4 nm • The molecules are aligned in rows oriented 45° • Along some edges the molecules are mismatched Molecular confinement • Some details: • Height of the islands ~ 0.6 nm (+ hole depth = 1 nm)

  16. • Regular rows: 3b ~ 1.4 nm • Distance between molecules in a row: 2b ~ 0.95 nm Matching the substrate... • Potential arrangement of the molecules : • Apparent size ~1 nm • Alignment along the [110] axis

  17. Electrostatic field inside a hole:  Understanding the trapping mechanism • A dipole d ~ 1 debye can be trapped at the corner site! • (U = d·E ~ 8 kBT)

  18. Interpretation • Expected arrangement of the molecules: • The sign of the corner site selects the growth direction • Dipole-dipole interaction ~ Dipole-substrate interaction • Both interactions are > kBT molecular confinement • Mismatch at edges due to 3-fold symmetry

  19. Empty vs filled holes • On larger scale... 150 nm • Only the holes < 15 nm in size are filled !

  20. Outlook • Molecules with 4-fold symmetry • How to contact electrodes? • Theory of molecular confinement? Conclusions • Holes created by e- irradiation on KBr act as molecular traps • Single organic molecules on insulators have been resolved by AFM • The size of the holes is critical

  21. This work was supported by • The Swiss National Science Fundation • The Swiss National Center of Competence in Research on Nanoscale Science Acknowledgments UNI Basel Ernst Meyer Christoph Gerber Laurent Nony Alexis Baratoff Roland Bennewitz (*) Oliver Pfeiffer Thomas Young University of Tokyo T. Eguchi CNRS Toulouse A. Gourdon C. Joachim (*) Now at McGill University, Montreal